PENGARUH KONSENTRASI ASAM SITRAT, SUHU, WAKTU, DAN PULP DENSITY PADA PELINDIAN COBALT DARI KATALIS BEKAS DENGAN METODE HIDROMETALURGI

JIHAN NABILAH , YULFIRA (2026) PENGARUH KONSENTRASI ASAM SITRAT, SUHU, WAKTU, DAN PULP DENSITY PADA PELINDIAN COBALT DARI KATALIS BEKAS DENGAN METODE HIDROMETALURGI. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG .

Preview	File PDF ABSTRAK.pdf Download (1760Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya staf Download (1825Kb) | Minta salinan
Preview	File PDF SKRIPSI TANPA PEMBAHASAN.pdf Download (1567Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Penelitian mengenai recovery logam cobalt (Co) dari katalis bekas hidrodesulfulrisasi menggunakan metode ekstraksi padat-cair telah dilakukan. Penelitian ini bertujuan untuk memperoleh bahan baku logam Co yang dapat digunakan kembali menggunakan ultrasonik pada variasi pulp density, suhu, konsentrasi asam sitrat, dan waktu pelindian terhadap kinetika reaksi pelindian cobalt sehingga dapat mengurangi masalah lingkungan yang timbul akibat limbah katalis bekas hidrodesulfurisasi. Metode ini dilakukan dengan pelindian duplo logam Co dari katalis bekas menggunakan Na 2 CO 3 1 M pada suhu 60°C dan pulp density 2,5% selama 2 jam yang dilanjutkan dengan pelindihan menggunakan asam sitrat dengan variasi pulp density, suhu, konsentrasi asam sitrat, dan waktu pelindian. Filtrat setelah pelindian dikarakterisasi dengan AAS dan residu pelindian dikarakterisasi dengan XRF. Hasil penelitian menunjukkan bahwa recovery logam Co dalam filtrat secara optimum sebesar 37,275% dan kandungan logam Co dalam residu dalam rentang sebesar 14,09−14,4% yang dilakukan dengan agen pelindi asam sitrat 1 M dengan pulp density 2,5% pada suhu 60°C selama 120 menit. Penelitian ini menggunakan model kinetika Shrinking Core (SCM). Hasil penelitian menunjukkan bahwa adanya indikasi difusi dalam mengendalikan laju pelindian dengan nilai R 2 dari analisis SCM sebesar 0,998 dan energi aktivasi yang negatif dari analisis Arrhenius sebesar 6,202 kJ mol −1 (30℃ − 60℃) dan −25,04 kJ mol −1 (60℃ − 80℃) yang menunjukkan bahwa pelindian tidak dikontrol oleh satu mekanisme (mixed control system) karena konstanta laju tidak meningkat secara konsisten. Kata kunci: cobalt, recovery, pelindian, Na2 CO3, asam sitrat, kinetika Research on the recovery of cobalt (Co) metal from spent hydrodesulfurization catalyst using solid-liquid extraction method has been conducted. This study aims to obtain reusable Co metal raw materials using ultrasonics at variations in pulp density, temperature, citric acid concentration, and leaching time on the kinetics of cobalt leaching reaction so as to reduce environmental problems arising from spent hydrodesulfurization catalyst waste. This method is carried out by duplo leaching of Co metal from spent catalyst using Na 2 CO 3 1 M at a temperature of 60°C and a pulp density of 2.5% for 2 hours followed by leaching using citric acid with variations in pulp density, temperature, citric acid concentration, and leaching time. The filtrate after leaching was characterized by AAS and the leaching residue was characterized by XRF. The results of the study showed that the optimum recovery of Co metal in the filtrate was 37.275% and the Co metal content in the residue was in the range of 14.09−14.4% which was carried out with a 1 M citric acid leaching agent with a pulp density of 2.5% at a temperature of 60°C for 120 minutes. This study used the Shrinking Core kinetics model (SCM). The research results show that there are indications of diffusion in controlling the leaching rate with an R 2 value from SCM analysis of 0.998 and a negative activation energy from Arrhenius analysis of sebesar 6.202 kJ mol −1 (30℃ − 60℃) and −25.04 kJ mol −1 (60℃ − 80℃) which indicates that leaching is not controlled by one mechanism (mixed control system) because the rate constant does not increase consistently. Keywords: cobalt, recovery, leaching, Na 2 CO 3 , citric acid, kinetic

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika 500 ilmu pengetahuan alam dan matematika > 540 Kimia dan ilmu yang berhubungan
Program Studi:	FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM (FMIPA) > Prodi S1 Kimia
Pengguna Deposit:	2605000131 Digilib
Date Deposited:	19 Jun 2026 03:23
Terakhir diubah:	19 Jun 2026 03:23
URI:	http://digilib.unila.ac.id/id/eprint/101061

Actions (login required)

Lihat Karya Akhir