KARAKTERISASI BAJA KARBON TINGGI AISI 1090 YANG DILAPISI ALUMINIUM DENGAN METODE CELUP PANAS (HOT DIPPING)

0615021124, YUSFIUL HILAL (2012) KARAKTERISASI BAJA KARBON TINGGI AISI 1090 YANG DILAPISI ALUMINIUM DENGAN METODE CELUP PANAS (HOT DIPPING). Other thesis, Universitas Lampung.

[img]
Preview
File PDF
ABSTRACT.pdf

Download (15Kb) | Preview
[img]
Preview
File PDF
ABSTRAK.pdf

Download (14Kb) | Preview
[img]
Preview
File PDF
BAB I.pdf

Download (24Kb) | Preview
[img]
Preview
File PDF
BAB II.pdf

Download (46Kb) | Preview
[img]
Preview
File PDF
BAB III.pdf

Download (14Kb) | Preview
[img] File PDF
BAB IV.pdf
Restricted to Hanya pengguna terdaftar

Download (115Kb)
[img]
Preview
File PDF
BAB V.pdf

Download (14Kb) | Preview
[img]
Preview
File PDF
DAFTAR ISI.pdf

Download (17Kb) | Preview
[img]
Preview
File PDF
RIWAYAT HIDUP.pdf

Download (14Kb) | Preview
[img]
Preview
File PDF
SANWACANA.pdf

Download (15Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Baja karbon tinggi AISI 1090 dilapisi dengan Al dengan metode celup panas pada temperatur 700 °C dengan variasi waktu pencelupan 9, 16 dan 25 detik. Analisa hasil celup panas baja karbon tinggi pada Al cair dilakukan dengan OM, SEM, XRD dan uji kekerasan. Dari hasil penelitian dan pengujian yang dilakukan tehadap baja karbon tinggi yang di hot dipping aluminizing coating dengan temperatur 700 °C diperoleh lapisan intermetalik yaitu FeAl 3 dan Fe Ketebalan lapisan Al meningkat pada permukaan substrat baja seiring dengan lamanya waktu pencelupan. Namun setelah pencelupan 16 detik ketebalan Al konstan hal ini dikarenakan adanya silikon yang terlarut dalam matriks Al.

Jenis Karya Akhir: Tesis (Other)
Subyek:
Program Studi: Fakultas Teknik > Prodi S1-Teknik Mesin
Pengguna Deposit: . . Yulianti
Date Deposited: 30 Jul 2015 08:34
Terakhir diubah: 30 Jul 2015 08:34
URI: http://digilib.unila.ac.id/id/eprint/11294

Actions (login required)

Lihat Karya Akhir Lihat Karya Akhir