STUDI KEMAMPUAN ADSORPSI KOMPLEKS cis-[Co(en) 2 (CN) 2].2H 2 O TERHADAP GAS NO2 MENGGUNAKAN MATRIKS PENDUKUNG ZEOLIT LAMPUNG

0617011051, Purwanto (2012) STUDI KEMAMPUAN ADSORPSI KOMPLEKS cis-[Co(en) 2 (CN) 2].2H 2 O TERHADAP GAS NO2 MENGGUNAKAN MATRIKS PENDUKUNG ZEOLIT LAMPUNG. Digital Library.

Preview	File PDF abstrak.pdf Download (481Kb) | Preview
Preview	File PDF bab 1.pdf Download (933Kb) | Preview
Preview	File PDF bab 3.pdf Download (1234Kb) | Preview
Preview	File PDF bab 2.pdf Download (7Mb) | Preview
	File PDF bab 4.pdf Restricted to Hanya pengguna terdaftar Download (3141Kb)
Preview	File PDF bab 5.pdf Download (281Kb) | Preview
Preview	File PDF cover.pdf Download (89Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Abstrak Telah disintesis senyawa kompleks cis-[Co(en) 2 (CN) 2].2H 2 O berwarna coklat tua dari campuran Co(CN) 2.6H 2 O dan etilendiamin (1:2) menggunakan pelarut etanol 95 % sebanyak 1,54 gram (rendemen 78,17 %). Hasil yang diperoleh dibuat pellet dengan menambahkan zeolit Lampung sebagai matriks pendukung dengan variasi komposisi kompleks-zeolit Lampung (b/b): 0:2; 1:0; 0,5:2; 0,3:2 dan 0,1:2 gram yang digunakan sebagai adsorben. Adsorben yang diperoleh berubah menjadi rapuh dan retak dari kondisi sebelumnya setelah diinteraksikan dengan gas NO 2 . Hasil analisis UV-Vis didapatkan nilai panjang gelombang maksimum dengan nilai berturut-turut 467, 466, 460 dan 461 nm pada sampel 1:0; 0,5:2; 0,3:2 dan 0,1:2. Dari data IR menunjukkan adanya serapan NO 2 di daerah bilangan gelombang 1500-1300 cm -1 sehingga dari kedua data tersebut dapat diasumsikan kompleks hasil interaksi memiliki struktur cis-[Co(en)(CN) 2(NO 2 ) 2].2H 2 O. Kata kunci: Kompleks, Zeolit, Adsorben Abstract It was synthesized a complex compound cis-[Co(en) 2 (CN) 2].2H 2 O dark brown from a mixture of Co(CN) 2.6H 2 O and ethylenediamine (1:2) of 1.54 g of using 95% ethanol solvent (yield 78.17%). The results obtained was made pellets with adding Lampung zeolit as a supporting matrix with the variation in the composition of complex - Lampung zeolit (w/w): 0:2; 1:0; 0.5:2; 0.3:2 and 0.1:2 gram used as adsorbent. Obtained adsorbents become brittle and crack from the previous condition after interaction with NO2 gas. Results of UV-Vis analys were obtained with the wavelength of maximum values 467, 466, 460 and 461 nm in the sample 1:0; 0.5:2; 0.3:2 and 0.1:2 respectively. From the IR data show existency of NO 2 absorption in the wavenumber region 1500-1300 cm-1. Therefore, from the both of data analys it may be assumed that interactions result complex has structure of cis-[Co (en)(CN) 2(NO 2 ) 2].2H 2 O. Keyword: Complex, Zeolit, Adsorben

Jenis Karya Akhir:	Artikel
Subyek:
Program Studi:	FAKULTAS MIPA > Prodi Kimia
Pengguna Deposit:	IC-STAR . 2015
Date Deposited:	22 Oct 2015 08:48
Terakhir diubah:	22 Oct 2015 08:48
URI:	http://digilib.unila.ac.id/id/eprint/13160

Actions (login required)

Lihat Karya Akhir