0617041049, JAYANTI DWI HAMDILA (2012) PENGARUH VARIASI MASSA TERHADAP KARAKTERISTIK FUNGSIONALITAS DAN TERMAL KOMPOSIT MgO-SiO BERBASIS SILIKA SEKAM PADI SEBAGAI KATALIS 2. Digital Library.
|
File PDF
TINJAUAN PUSTAKAA.pdf Download (495Kb) | Preview |
|
|
File PDF
TINJAUAN PUSTAKA.pdf Download (488Kb) | Preview |
|
|
File PDF
PENDAHULUAN.pdf Download (24Kb) | Preview |
|
|
File PDF
METODOLOGI PENELITIAN.pdf Download (34Kb) | Preview |
|
|
File PDF
LEMBAR PENGESAHAN.pdf Download (33Kb) | Preview |
|
|
File PDF
kesimpulan.pdf Download (8Kb) | Preview |
|
![[img]](http://digilib.unila.ac.id/style/images/fileicons/text.png) |
File PDF
HASIL N PEMBAHASAN.pdf Restricted to Hanya pengguna terdaftar Download (615Kb) |
|
|
File PDF
HALAMAN PENGESAHAN.pdf Download (5Kb) | Preview |
|
|
File PDF
HALAMAN DEPAN.pdf Download (144Kb) | Preview |
|
|
File PDF
COVER Depan.pdf Download (30Kb) | Preview |
|
|
File PDF
COVER.pdf Download (30Kb) | Preview |
|
|
File PDF
ABSTRAK.pdf Download (11Kb) | Preview |
|
|
File PDF
ABSTRACT.pdf Download (15Kb) | Preview |
Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)
Abstrak Telah dilakukan penelitian tentang fungsionalitas dan termal komposit MgO-SiO sebagai katalis dengan variasi massa MgO dan SiO sebesar 40:60, 50:50 dan 60:40. Pembuatan MgO-SiO 2 2 memanfaatkan magnesium nitrat heksahidrat sebagai sumber MgO dan silika sekam padi, menggunakan metode sol-gel dan perlakuan sintering 900ºC. Adapun, MgO-SiO dikarakterisasi menggunakan FTIR, DTA/TGA dan uji katalis. Hasil FTIR menunjukkan pada sampel sebelum dan sesudah sintering terbentuk gugus fungsi utama yakni Si-O-Si, Mg-O-Si, dan Mg-O. Massa MgO yang semakin besar mengakibatkan pembentukkan gugus Mg-O-Si dan Mg-O semakin meningkat dan gugus Si-O-Si semakin menurun, sedangkan semakin besarnya massa SiO 2 2 mengakibatkan pembentukkan gugus Si-O-Si semakin meningkat dan menurunnya gugus Mg-O-Si dan Mg-O. Hasil analisis DTA/TGA menunjukkan bahwa sampel mengalami reaksi endotermik dan eksotermik. Penyerapan panas (endoterm) lebih mudah terjadi seiring dengan penambahan massa MgO, namun kestabilan termal dicapai oleh sampel dengan massa silika terbesar yang ditandai oleh perubahan berat yang tidak terlalu signifikan. Hasil analisis FTIR dan DTA/TGA menunjukkan komposit MgO-SiO dapat diaplikasikan sebagai katalis. Hasil pengujian katalis menghasilkan senyawa utama metil laurat, metil miristat dan metil palmitat sebagai komponen biodiesel yang dihasilkan dari minyak kelapa. Kata kunci: sekam padi, MgO-SiO 2 , sol-gel, FTIR, DTA/TGA. 2 2 Abstract This research has been done about functionality and thermal of MgO-SiO composite as a catalyst with MgO and SiO mass variation of 40:60, 50:50 and 60:40. The making of MgO-SiO 2 2 benefited magnesium nitrate hexahydrate as source of MgO and rice husk silica, used sol-gel method and sintering at 900ºC. As for, MgO-SiO is characterized by FTIR, DTA/TGA and catalyst test. The result of FTIR showed to the sample of before and after sintering formed the main functional groups were Si-O-Si, Mg-O-Si and Mg-O. The greater mass of MgO resulted in an increased formation of Mg-O-Si and Mg-O groups and Si-OSi groups decreased, whereas the greater mass of SiO 2 resulted in an increased formation of Si-O-Si groups and decreased in Mg-O-Si and Mg-O groups. The result of DTA/TGA analysis showed that the sample experienced endothermic and exothermic reactions. The heat absorption occurred easily along with the addition of MgO mass but thermal stability was achieved by the most mass silica who marked with mass change was not significant. The analysis result of FTIR and DTA/TGA showed that MgO-SiO 2 2 composite can be applied to catalyst. The result of catalyst test showed the main compound such as methyl laurate, methyl miristate and methyl palmitate as biodiesel component who was resulted from coconut oil. Key words: rice husks, MgO-SiO 2 , sol-gel, FTIR, DTA/TGA, biodiesel. 2
| Jenis Karya Akhir: | Artikel |
|---|---|
| Subyek: | |
| Program Studi: | FAKULTAS MIPA > Prodi Biologi |
| Pengguna Deposit: | IC-STAR . 2015 |
| Date Deposited: | 22 Oct 2015 08:49 |
| Terakhir diubah: | 22 Oct 2015 08:49 |
| URI: | http://digilib.unila.ac.id/id/eprint/13171 |
Actions (login required)
 |
Lihat Karya Akhir |