0817041051, Revy Susi Maryanti (2012) Sintesis dan Karakterisasi Titania Silika Berbasis Titanium Butoksida dan Silika Sekam Padi dengan Metode Sol Gel. Digital Library.
|
File PDF
abstrak english.pdf Download (80Kb) | Preview |
|
|
File PDF
Abstrak.pdf Download (5Kb) | Preview |
|
|
File PDF
cover.pdf Download (13Kb) | Preview |
|
|
File PDF
I.pdf Download (93Kb) | Preview |
|
|
File PDF
II.pdf Download (432Kb) | Preview |
|
|
File PDF
III.pdf Download (198Kb) | Preview |
|
![[img]](http://digilib.unila.ac.id/style/images/fileicons/text.png) |
File PDF
IV.pdf Restricted to Hanya pengguna terdaftar Download (1231Kb) |
|
|
File PDF
KATA PENGANTAR.pdf Download (220Kb) | Preview |
|
|
File PDF
kata pengantar2.pdf Download (80Kb) | Preview |
|
|
File PDF
pengesahan.pdf Download (81Kb) | Preview |
|
|
File PDF
RIWAYAT HIDUP.pdf Download (93Kb) | Preview |
|
|
File PDF
riwayat hidup2.pdf Download (144Kb) | Preview |
|
|
File PDF
V.pdf Download (82Kb) | Preview |
Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)
Abstrak Telah dilakukan penelitian tentang komposit titania silika berbasis titanium butoksida dan silika sekam padi dengan variasi penambahan dopan silika pada titania. Dengan prosedur preparasi sampel, pressing, kalsinasi. Karakterisasi menyangkut XRD, SEM-EDS, uji fotokatalis, dan resistivitas. Hasil XRD TiO2- SiO2 menunjukkan bahwa pada perbandingan 1:1 menghasilkan fasa anatase dan struktur amorf. Hasil SEM menunjukkan mikrostruktur TiO2-SiO2 berubah seiring dengan perbandingan TiO2 dan SiO2. Hasil EDS menunjukkan unsur-unsur yang teridentifikasi dari komposit TiO2-SiO2, yaitu titanium, oksigen, silikon dan sedikit karbon. Hasil uji fotokatalis menunjukkan bahwa secara keseluruhan daya urai/degradasi pada cahaya ultraviolet relatif sama dengan cahaya tampak. Penguraian terbaik terdapat pada perbandingan komposisi titania silika 1:0,05 baik menggunakan metilen biru maupun metilen jingga. Resistivitas sampel makin turun seiring dengan menurunnya perbandingan komposisi silika. Kata Kunci : Fotokatalis, Resistivitas, SEM-EDS, SiO2, TiO2, XRD. Abstract The research of titania silica composite base on titanium butoxide and rice husk with various silica dopant increased in titania has been done. The preparation sampel are pressing and calsination. Sample characterization include XRD, SEM, phocatalyst test and resistivity. The result of XRD for 1:1 ratio sample showed antase fase and the amorph structure. Result of SEM characterization showed change of microstructure of TiO2-SiO2 compatible to comparison of silica in titania and EDS indicated the elements in the TiO2-SiO2 composite namely are titannium, oksigen, silicon, and a litle bit carbon. The photocatalyst result showed over all of sample degradation are relative the same used in UV and visible light. The best degradation of photocatalyst test showed in 1:0,05 comparison in the methylene blue and the methylen orange. Sample resistivity decreases with the decreasing ratio of silica composition. Key Word: photocatalyst, Resistivity, SEM-EDS, SiO2, TiO2, XRD
| Jenis Karya Akhir: | Artikel |
|---|---|
| Subyek: | |
| Program Studi: | FAKULTAS MIPA > Prodi Fisika |
| Pengguna Deposit: | IC-STAR . 2015 |
| Date Deposited: | 05 Nov 2015 06:44 |
| Terakhir diubah: | 05 Nov 2015 06:44 |
| URI: | http://digilib.unila.ac.id/id/eprint/14351 |
Actions (login required)
 |
Lihat Karya Akhir |