BONDAN SUDIANTO, 1015021024 (2015) AUS PAHAT POTONG DAN STRUKTUR MIKRO MAGNESIUM AZ31 PADA KONDISI PENGEFRAISAN KERING. Fakultas Teknik, Universitas Lampung.
|
Text
ABSTRACT.pdf Download (83kB) | Preview |
|
|
Text
ABSTRAK.pdf Download (6kB) | Preview |
|
|
Text
COVER DALAM.pdf Download (13kB) | Preview |
|
|
Text
COVER LUAR.pdf Download (17kB) | Preview |
|
|
Text
DAFTAR GAMBAR.pdf Download (86kB) | Preview |
|
|
Text
DAFTAR ISI.pdf Download (154kB) | Preview |
|
|
Text
DAFTAR TABEL.pdf Download (150kB) | Preview |
|
|
Text
LEMBAR PENGESAHAN.pdf Download (266kB) | Preview |
|
|
Text
LEMBAR PERNYATAAN.pdf Download (217kB) | Preview |
|
|
Text
LEMBAR PERSETUJUAN.pdf Download (271kB) | Preview |
|
|
Text
SANWACANA.pdf Download (11kB) | Preview |
|
|
Text
RIWAYAT HIDUP.pdf Download (14kB) | Preview |
|
|
Text
MOTO.pdf Download (61kB) | Preview |
|
|
Text
BAB I.pdf Download (29kB) | Preview |
|
|
Text
BAB II.pdf Download (285kB) | Preview |
|
|
Text
BAB III.pdf Download (129kB) | Preview |
|
![[img]](http://digilib.unila.ac.id/style/images/fileicons/text.png) |
Text
BAB IV.pdf Restricted to Registered users only Download (239kB) |
|
|
Text
BAB V.pdf Download (17kB) | Preview |
|
|
Text
DAFTAR PUSTAKA.pdf Download (21kB) | Preview |
Abstract
Penggunaan magnesium sebagai bahan alternatif pengganti besi dan baja telah mulai dilakukan saat ini. Proses pemesinan dideskripsikan sebuah proses penghilangan material. Proses pemesinan dikerjakan pada beberapa parameter tertentu. Parameter pemesinan terdiri dari gerakan makan, kecepatan potong, dan kedalaman potong. Adapun tujuan dari penelitian ini adalah untuk mengetahui efek pemesinan dari pengaruh parameter pemotongan terhadap umur pahat dan mendapatkan pengaruh dari parameter kecepatan potong terhadap perubahan struktur mikro magnesium. Pengujian keausan pahat dilakukan dengan menggunakan mikroskop. Pengujian struktur mikro menggunakan mikroskop dengan perbesaran 100X. Pada pengujian keausan, RO (Run Order) ke 6 mendapatkan nilai umur pahat yang sangat cepat yaitu selama 5 menit dengan kecepatan potong 42,7 m/min, gerak pemakanan 0,25 mm/rev dan kedalaman potong 3 mm. Pada RO (Run Order) ke 5 mendapatkan nilai umur pahat yang sangat lama, yaitu selama 77 menit dengan kecepatan potong 22,86 m/min, gerak pemakanan 0,15 mm/rev dan kedalaman potong 1 mm. Pada pengujian struktur mikro, magnesium yang mengalami proses pemesinan tidak mengalami perubahan struktur mikro. Dengan hal ini dapat disimpulkan bahwa kecepatan potong pada pemesinan frais tidak menimbulkan pengaruh terhadap struktur mikro magnesium. Kata Kunci : MgAZ31, Mesin Frais, Pahat HSS diameter 8mm, Cairan Etsa, Mikroskop USB ABSTRACT CHISEL WORN-OUT AND MAGNESIUM MICRO STRUCTURE ON DRY MILLING CONDITION Using magnesium as the steel and iron for the alternative way has been do as far until this decade. The engineer process is describe a process about material loosing. engineer process worked for a few parameter. Mechanical parameter coming from feed rate, cutting speed and deep of cutting. The purpose of this research is to test about engine efect from parameter cutting influence for chisel and micro magnesium structure. Worn-out testing can be test with microscope. Micro structure test by microscope with 100 times magnification. On worn-out test, the six Run Order (RO) got the longest faster time chisel, in 5 minute with cutting speed about 42,7 m/t, feed rate 0,25 mm/rev and deep of cutting 3 mm. In the 5 Run Order (RO) got the slowest, 77 minute with 22,86 m/t speed of cutting, 0,15 feed rate and 1mm deep of cutting. On micro structure test magnesium have no micro structure changing. In this research the conclution if cutting speed on engine milling process is not influential for micro magnesium structure. Keyword : MgAZ31, MILLING ENGINE, CHISEL 8MM d., ETCHING LIQUID, USB MICROSCOPE
| Item Type: | Other |
|---|---|
| Subjects: | Teknologi > Teknik mesin dan mesin Teknologi > Teknik mesin dan mesin |
| Divisions: | Fakultas Teknik > Prodi Teknik Mesin |
| Depositing User: | 5661639 . Digilib |
| Date Deposited: | 29 Dec 2015 07:40 |
| Last Modified: | 29 Dec 2015 07:40 |
| URI: | http://digilib.unila.ac.id/id/eprint/16301 |
Actions (login required)
 |
View Item |