NN, M.M. ADITYA SESUNAN (2012) PENGARUH ADITIF ARANG TEMPURUNG KELAPA SEBAGAI PENGGANTI MATERIAL FILLER TERHADAP DURABILITAS CAMPURAN ASPAL. Digital Library.
|
File PDF
1. Abstrak M.M. Aditya Sesunan 0415011019.pdf Download (89Kb) | Preview |
|
|
File PDF
9. Pendahuluan Adit MM Sip.pdf Download (278Kb) | Preview |
|
|
File PDF
13. Simpulan dan Saran Adit MM Sip.pdf Download (87Kb) | Preview |
Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)
Abstract Durabilitas (Durability) adalah keawetan atau daya tahan terhadap rusak akibat pengaruh buruk cuaca dan lalu lintas. Tujuan dari penelitian ini adalah untuk mengetahui pengaruh volume pengganti material filler Arang Tempurung Kelapa (ATK) terhadap durabilitas campuran aspal. Penelitian dimulai dari pembuatan benda uji dengan kadar aspal 4,5%, 5,0%, 5,5,%, 6,0%, dan 6,5%, yang dipadatkan menggunakan pemadatan Marshall dengan 4 macam variasi persen pengganti filler ATK 0%, 33,3%, 66,7%, dan 100%, kemudian diuji lebih lanjut dengan uji perendaman pada kadar aspal optimum. Hasil penelitian menunjukkan bahwa dengan penggantian filler ATK memiliki pengaruh yang baik terhadap peningkatan nilai stabilitas campuran aspal. Nilai rongga udara dalam campuran (VIM) juga semakin meningkat seiring dengan penambahan persen kadar ATK. Kadar Aspal Optimum (KAO) menunjukkan bahwa semakin besar kadar ATK maka nilai stabilitas akan meningkat, sampai pada titik tertentu penambahan kadar ATK akan menurunkan nilai stabilitas. Indeks Kekuatan Sisa (IKS) yang dihasilkan memperlihatkan bahwa ternyata terdapat pengaruh negatif dari air terhadap durabilitas campuran aspal. Kata kunci : ATK, carbon black, durability, marshall test, immersion test Pembimbing I : Sasana Putra, S.T., M.T. Pembimbing II : Taharuddin, S.T., M.Sc. Penguji Utama : Ir. Priyo Pratomo, M.T. Abstract Durability is the resistance of destruction that caused by the bad weather and the traffic. The research purpose are to determine the replacement volume effect of filler material of Charcoal Coconut-Shell (CCS) on durability of asphalt mixtures. This research is started from manufacture the sample with variation of asphalt content, there are 4.5%, 5.0%, 5.5%, 6.0%, and 6.5%, which were compacted using Marshall’s compaction with four kinds of variation percent filler substitution of CCS 0%, 33.3%, 66.7%, and 100%, then examined further by immersion test at optimum asphalt content. The results show that the replacement CCS filler gives a good effect to increase the stability of asphalt mixtures. The value of air voids in mix (VIM) also increased when the addition of percent levels of CCS was increased. Optimum asphalt content (OAC) show that when CCS levels was increased, the value of stability also increase, until at some point of the addition of CCS levels was reduced the value of stability. Index retained of stability (IRS) values was show a negative influence of water on the durability of asphalt mixtures. Keywords : ATK, carbon black, durability, marshall test, immersion test
| Jenis Karya Akhir: | Artikel |
|---|---|
| Subyek: | |
| Pengguna Deposit: | tik 15 . Digilib |
| Date Deposited: | 15 Jan 2016 08:15 |
| Terakhir diubah: | 15 Jan 2016 08:15 |
| URI: | http://digilib.unila.ac.id/id/eprint/18402 |
Actions (login required)
 |
Lihat Karya Akhir |