KONVERSI SELULOSA MENJADI GULA ALKOHOL MENGGUNAKAN KATALIS LaCr0,7Mo0,3O3±δ

Surtini Karlina Sari, 1017011016 (2016) KONVERSI SELULOSA MENJADI GULA ALKOHOL MENGGUNAKAN KATALIS LaCr0,7Mo0,3O3±δ. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK (ABSTRACT).pdf Download (329Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya pengguna terdaftar Download (4Mb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (3304Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Pada penelitian ini, katalis LaCr0,7Mo0,3O3±δ telah dipreparasi menggunakan metode sol-gel dan pektin sebagai agen pengemulsi, dilanjutkan dengan kalsinasi pada temperatur 600 dan 700 oC. Katalis telah dikarakterisasi dengan teknik yang berbeda. Katalis digunakan untuk uji konversi selulosa menjadi gula alkohol pada temperatur 100, 120 dan 140 oC serta aliran gas H2 50 ml/menit dari awal proses hidrolisis selulosa selama 1, 2 dan 3 jam. Analisis keasaman dengan metode gravimetri, mengungkapkan bahwa katalis LaCr0,7Mo0,3O3±δ memiliki keasaman 6,36 dan 6,17 mmol piridin/gram pada katalis yang telah dikalsinasi 600 dan 700 oC. Berdasarkan metode Fourier Transform Infra Red (FTIR) situs asam Lewis lebih dominan. Hasil analisis difraksi sinar-X (XRD) katalis terdiri dari beberapa fasa kristal yakni fasa La2(MoO4)3, LaCrO3, dan sedikit LaCrO4 dengan fasa kristal terbanyak berupa LaCrO3 pada katalis 700 oC. Hasil analisis morfologi katalis dengan metode Transmission Electron Microscop (TEM) menunjukkan morfologi permukaan yang heterogen. Hasil analisis distribusi ukuran partikel dengan metode Particle Size Analyzer (PSA) menunjukkan adanya nanopartikel dengan jumlah relatif 15,35% pada kalsinasi 600 oC dan 13,38 % pada kalsinasi 700 oC. Uji Fehling mengindikasikan bahwa hasil terbaik diperoleh menggunakan aliran gas H2 50 ml/menit dan waktu hidrolisis 2 jam. Analisis menggunakan High Performance Liquid Chromatography (HPLC) mengungkapkan bahwa selulosa dikonversi menjadi mannitol dengan konsentrasi tertinggi sebesar 30504,58 ppm dihasilkan dari eksperimen pada kondisi 100 oC, menggunakan katalis yang dikalsinasi pada 700 oC. CELLULOSE CONVERSION INTO SUGAR ALCOHOL USING THE CATALYST LaCr0,7Mo0,3O3 ± δ In this study, LaCr0,7Mo0,3O3 ± δ catalysts were prepared using sol-gel method and pectin as an emulsifying agent, followed by calcination at 600 and 700 oC. The catalysts were characterized using different techniques. The catalysts were then tested for conversion of cellulose into alcohol sugars at different temperatures of 100, 120 and 140 oC and 50 ml/min H2 gas flow, for different times of 1, 2, and 3 hours. The acidity by gravimetric methods revealed that LaCr0,7Mo0,3O3 ± δ catalysts have acidity of 6.36 and 6.17mmol pyridine/gram of catalysts calcined at 600 and 700 oC, respectively. According to Fourier Transform Infra Red (FTIR) method the Lewis acid sites are predominant. The results of the analysis of X-ray diffraction (XRD) indicated that catalyst comprises several crystalline phase, including La2(MoO4)3, LaCrO3, and LaCrO4 with the highest crystallinity of LaCrO3 exhibited by the catalyst calcined at 700 oC catalyst. The results of morphology analysis using Transmission Electron Microscop (TEM) method shows heterogeneous morphology of the surface. The results of the particle size distribution analysis by Particle Size Analyzer (PSA) demonstrated the presence of nano-particles with the relative amount of 15.35% in the catalyst calcinated at 600 oC and 13.38% in the catalyst calcinated at 700 oC. Fehling test indicated that the best result was obtained using 50 ml/min H2 gas flow and hydrolysis time for 2 hours. Analysis using High Performance Liquid Chromatography (HPLC) revealed that cellulose was converted into mannitol with the highest concentration of 30504.58 ppm produced from the experiment carried out at 100 oC, using the catalyst calcined at 700 oC.

Jenis Karya Akhir:	Skripsi
Subyek:	> QD Chemistry
Pengguna Deposit:	4795448 . Digilib
Date Deposited:	07 Apr 2016 04:47
Terakhir diubah:	07 Apr 2016 04:47
URI:	http://digilib.unila.ac.id/id/eprint/21634

Actions (login required)

Lihat Karya Akhir