SINTESIS DAN KARAKTERISASI SERTA UJI AKTIVITAS ANTIKOROSI SENYAWA TURUNAN ORGANOTIMAH(IV) BENZOAT TERHADAP BAJA LUNAK DALAM MEDIUM KOROSIF NACl

SUKAMTO , 1217011056 (2016) SINTESIS DAN KARAKTERISASI SERTA UJI AKTIVITAS ANTIKOROSI SENYAWA TURUNAN ORGANOTIMAH(IV) BENZOAT TERHADAP BAJA LUNAK DALAM MEDIUM KOROSIF NACl. FAKULTAS MATEMATIKA ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK (ABSTRACT).pdf Download (162Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya pengguna terdaftar Download (3966Kb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (2709Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Pada penelitian ini telah dilakukan sintesis senyawa difeniltimah(IV) dibenzoat dan trifeniltimah(IV) benzoat dengan cara mereaksikan senyawa awal difeniltimah(IV) oksida dan trifeniltimah(IV) hidroksida dengan asam benzoat sebagai ligannya. Kedua senyawa yang diperoleh berupa serbuk berwarna putih dengan rendemen masing-masing 89,49% dan 83,51%. Senyawa hasil sintesis telah divalidasi dengan spektrofotometer IR, UV-Vis dan microelemental analyzer. Senyawa hasil sintesis selanjutnya diuji aktivitas antikorosinya terhadap baja lunak dalam medium korosif larutan NaCl dengan metode potensiodinamik menggunakan instrumentasi ER410 Integrated Potensiostat System eDAQ. Hasil pengujian menggunakan metode potensiodinamik menunjukkan bahwa senyawa difeniltimah(IV) dibenzoat dan trifeniltimah(IV) benzoat memiliki kemampuan yang baik dalam menghambat proses korosi yang terjadi pada baja lunak dengan nilai persentase inhibisi tertinggi masing-masing 77,4% dan 79,79% pada konsentrasi 100 mg/L serta nilai laju korosi sebesar 1,37 Rmpy dan 1,26 Rmpy. Kata Kunci : antikorosi, baja lunak, potensiodinamik, organotimah(IV) benzoat abstract In this research, the synthesis of diphenyltin(IV) dibenzoate and triphenyltin(IV) benzoate have been performed by the reaction between diphenyltin(IV) oxide and triphenyltin(IV) hydroxide with benzoic acid as a ligand. Both of the compounds were produced as white solid with the yield of 89.49% and 83.51%, respectively. The yields were validated using infrared, UV-Vis spectroscopies and microelemental analyzer. The compounds synthesized were tested of the corrosion activity towards hot roller plate (HRP) mild steel in the corrosive medium of NaCl by potentiodynamic method using ER410 Integrated Potensiostat System eDAQ. The result showed that diphenyltin(IV) dibenzoate and triphenyltin(IV) benzoate have good ability to prevent corrosion process on the mild steel with the highest percentage of inhibition at concentration at 100 mg/L were 77.4% and 79.79% and the rate of corrosion were 1,37 Rmpy and 1,26 Rmpy, respectively. Keywords: anticorrosion, mild steel, potentiodynamic, organotin(IV) benzoate

Jenis Karya Akhir:	Skripsi
Subyek:	> Q Science (General)
Program Studi:	FAKULTAS MIPA > Prodi Kimia
Pengguna Deposit:	26712951 . Digilib
Date Deposited:	10 May 2016 03:57
Terakhir diubah:	10 May 2016 03:57
URI:	http://digilib.unila.ac.id/id/eprint/22232

Actions (login required)

Lihat Karya Akhir