KARAKTERISTIK SIFAT TERMAL (DTA-TGA) DAN KONDUKTIVITAS TERMAL KERAMIK CORDIERITE BERBASIS SILIKA SEKAM PADI DENGAN PENAMBAHAN ALUMINA (0, 20, 25 DAN 30 WT%)

Dita Rahmayanti, 1117041009 (2016) KARAKTERISTIK SIFAT TERMAL (DTA-TGA) DAN KONDUKTIVITAS TERMAL KERAMIK CORDIERITE BERBASIS SILIKA SEKAM PADI DENGAN PENAMBAHAN ALUMINA (0, 20, 25 DAN 30 WT%). UNIVERSITAS LAMPUNG, FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM .

[img]
Preview
Text
ABSTRAK (ABSTRACT).pdf

Download (9Kb) | Preview
[img] Text
SKRIPSI FULL.pdf
Restricted to Registered users only

Download (990Kb)
[img]
Preview
Text
SKRIPSI TANPA BAB PEMBAHASAN.pdf

Download (991Kb) | Preview

Abstrak

Penelitian ini dilakukan untuk mengetahui karakteristik sifat termal (DTA-TGA) dan konduktivitas termal keramik cordierite berbasis silika sekam padi dengan penambahan alumina 0, 20, 25 dan 30 wt%. Cordierite disintesis menggunakan silika yang berasal dari sekam padi menggunakan metode sol-gel, MgO dan Al2O3. Pencampuran cordierite-alumina dilakukan dengan metode reaksi padatan dan disintering pada suhu 1200oC. Hasil analisis pengukuran karakteristik sifat termal menggunakan Differential Thermal Analysis (DTA) sampel C0, C20, C25, dan C30 pembentukan kristal kristobalit dan kristal spinel pada puncak eksotermal 694, 655, 672, dan 671oC. Pada pengukuran Thermalgrafimetric Analysis (TGA) sampel C20 yang mengalami total kehilangan massa terendah sebesar 0.292% dan kehilangan massa terbesar sampel C30 yaitu, 3.436%. Sementara, hasil analisis konduktivitas termal membuktikan semakin meningkat presentase alumina, maka konduktivitas termal meningkat, yaitu 11.34 – 15.59 W/m.K. Konduktivitas termal cordierite-alumina mengindikasi serupa dengan konduktivitas termal dari fasa spinel. Kata kunci: Alumina, cordierite, DTA, konduktivitas termal, silika sekam padi, spinel, dan TGA. abstract This study was conducted to determine the characteristics of the thermal properties (DTA-TGA) and thermal conductivity of cordierite ceramic silica-based rice husk with the addition of alumina 0, 20, 25 and 30 wt%. Cordierite synthesized using silica derived from rice husk using sol-gel method, MgO and Al2O3. Mixing cordierite-alumina was conducted using solid state reaction and sintering at a temperature of 1200oC. The results of the analysis of the characteristics measurement of thermal properties using Differential Thermal Analysis (DTA) of samples C0, C20, C25, and C30 formation of cristobalite crystals and spinel crystals on the exothermic peaks 694, 655, 672, and 671oC. In measurement Thermalgrafimetric Analysis (TGA) of samples C20 experiencing the lowest total mass loss amounted to 0.292% and the largest mass loss of samples C30 that is, 3.436%. Meanwhile, the thermal conductivity analysis results prove the increasing percentage of alumina, the thermal conductivity increases, ie 11.34 - 15.59 W/m.K. The thermal conductivity indicate cordierite-alumina similar to the thermal conductivity of the spinel phase. Keywords: Alumina, cordierite, DTA, TGA, thermal conductivity, silica rice husk, and spinel.

Tipe Karya Ilmiah: Skripsi
Subyek: Q Science (General)
Program Studi: Fakultas MIPA > Prodi Fisika
Depositing User: 8007834 . Digilib
Date Deposited: 18 Oct 2016 03:55
Last Modified: 18 Oct 2016 03:55
URI: http://digilib.unila.ac.id/id/eprint/24069

Actions (login required)

View Item View Item