STUDI KONDUKTIVITAS LISTRIK ZEOLIT AKIBAT PENGARUH MIKROSTRUKTUR DAN LUAS PERMUKAAN SPESIFIK SERTA POTENSINYA SEBAGAI ELEKTRODE SUPERKAPASITOR

JENNIFER KAPRIATI PAKAPAHAN , (1217041024) (2016) STUDI KONDUKTIVITAS LISTRIK ZEOLIT AKIBAT PENGARUH MIKROSTRUKTUR DAN LUAS PERMUKAAN SPESIFIK SERTA POTENSINYA SEBAGAI ELEKTRODE SUPERKAPASITOR. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK (ABSTRACT).pdf Download (36Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya pengguna terdaftar Download (1745Kb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (1631Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

ABSTRAK Telah dilakukan penelitian mengenai studi konduktivitas listrik sintesis zeolit berbasis silika sekam padi menggunakan metode sol-gel akibat pengaruh mikrostruktur dan luas permukaan spesifik dengan perlakuan termal 450 oC, 550 oC, dan 650 oC. Pengujian yang dilakukan meliputi penentuan struktur fasa menggunakan X-Ray Diffraction (XRD), mikrostruktur menggunakan Scanning Electron Microscope (SEM), luas permukaan spesifik menggunakan analisis Branauer Emmet Teller (BET), dan konduktivitas dengan LCR meter. Hasil XRD memperlihatkan bahwa struktur berbentuk amorf dengan fasa kristobalit, korundum, dan delta-Al2O3. Perlakuan termal 450 oC - 650 oC menjadikan ukuran butir dan partikel meningkat sementara ukuran pori menurun dilihat dari karakterisasi SEM. Pada perlakuan termal 450 oC menunjukkan ukuran butir paling kecil yaitu 3,691 μm dan partikel sebesar 16,322 μm sementara ukuran pori paling besar yaitu 5,786 μm. Hasil analisis BET menunjukkan nilai luas permukaan spesifik zeolit dengan perlakuan termal 450 oC - 650 oC adalah 149,98 m2/g hingga 216,25 m2/g. Hasil LCR meter menunjukkan nilai konduktivitas sampel 0,9613x10-3 S/cm hingga 1,2727x10-3 S/cm, dimana konduktivitas ini memperlihatkan bahwa zeolit merupakan bahan semikonduktor. Besar luas permukaan dan konduktivitas memiliki potensi untuk digunakan sebagai elektrode superkapasitor. Kata kunci: Konduktivitas listrik, luas permukaan spesifik, mikrostruktur, perlakuan termal, dan zeolit. ASTRACT Study of electrical conductivity zeolite synthesis based rice husk silica using solgel methode due to effect of microstructure and specific surface area with heat treatment 450 oC, 550 oC, dan 650 oC has been investigated. The characteristics of sample were observed from phase structure through by X-Ray Difraction (XRD), microstructure through Scanning Electron Microscopy (SEM), specific surface area through Branauer Emmet Teller (BET), and conductivity through LCR meter. The result of XRD showed that structure was amorph with cristobalite, corundum, and delta-Al2O3 phase. The heat treatment of 450 oC - 650 oC made the grain size and particle increase while pore size decrease had seen from SEM characterization. In the thermal treatment of 450 °C showed the smallest grain size is 3,691 μm and particel amounted to 16,322 μm while the large pore size is 5,786 μm. BET analysis results showed the value of spesific surface area of zeolite with heat treatment 450 oC - 650 oC was 149,98 m2/g to 216,25 m2/g. Condutivity obtained from LCR meter showed that its value from 9613x10-3 S/cm to 1,2727x10-3 S/cm, indicating that zeolite is a semiconductor material. The large surface area and conductivity has potential to be used as a supercapacitor electrode. Keywords: Electrical Conductivity, heat treatment, specific surface area, microstructure, and zeolite.

Jenis Karya Akhir:	Skripsi
Subyek:	> QC Physics
Program Studi:	FAKULTAS MIPA > Prodi Fisika
Pengguna Deposit:	0419729 . Digilib
Date Deposited:	27 Oct 2016 04:39
Terakhir diubah:	27 Oct 2016 04:39
URI:	http://digilib.unila.ac.id/id/eprint/24313

Actions (login required)

Lihat Karya Akhir