PEMBUATAN DAN KARAKTERISASI NANOKATALIS Ni0,6Cu0,4Fe2O4 SERTA UJI AKTIVITAS PADA KONVERSI (CO2 + H2)

Feby Rinaldo Pratama Kusuma, 1217011022 (2016) PEMBUATAN DAN KARAKTERISASI NANOKATALIS Ni0,6Cu0,4Fe2O4 SERTA UJI AKTIVITAS PADA KONVERSI (CO2 + H2). FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRACT (ABSTRAK).pdf Download (149Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya pengguna terdaftar Download (3106Kb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (3106Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Telah dilakukan pembuatan nanokatalis Ni0,6Cu0,4Fe2O4 pada kalsinasi 600°C dan 800°C, dengan metode sol-gel menggunakan pengemulsi pektin, serta dilakukan uji aktivitas katalitik terhadap hasil konversi gas (CO2 + H2) menjadi alkohol pada suhu reaksi 200°C, 250°C, dan 300°C. Analisis keasaman katalis didapatkan penyerapan sebesar 0,68773 mmol piridin/g katalis pada kalsinasi 600°C dan 0,605125 mmol piridin/g katalis pada kalsinasi 800°C. Karakterisasi ukuran partikel (XRD) dan distribusi ukuran butiran (PSA) diproleh rata-rata ukuran partikel 16,02 nm dengan distribusi ukuran partikel 60% kalsinasi 600°C dan 26,64 nm dengan distribusi ukuran partikel 35% kalsinasi 800°C. SEM – EDS menyatakan bahwa terdapat unsur O, Fe, Ni, dan Cu yang menunjukkan terbentuknya senyawa Ni0,6Cu0,4Fe2O4. Analisis menggunakan kromatografi gas menyatakan bahwa katalis Ni0,6Cu0,4Fe2O4 pada suhu kalsinasi 600°C dengan suhu reaksi 200°C dan 300°C memiliki keaktifan tinggi terhadap konversi (CO2 + H2) menghasilkan etanol sebesar 0,1992% dan 0,2752%. Kata kunci: nanokatalis, metode sol-gel, konversi (CO2 + H2), pektin, alkohol. ABSTRACT In this study, nanocatalyst Ni0,6Cu0,4Fe2O4 has been prepared by sol-gel method using pectin as an emulsifying agent, and then the sample was subjected to calcination treatment at 600oC and 800oC. Its catalytic activity was tested for CO2/H2 conversion to alcohol at temperature of 200, 250, and 300°C. Analysis of the catalyst’s acidity showed pyridine absorption at 0.68773 mmol/g catalyst at calcination temperature 600oC and 0.605125 mmol/ g catalyst at calcination temperature 800oC. X-ray diffraction (XRD) and particle size analyzer (PSA) of catalyst showed that particle size is 16,02 nm with 60%size distribution at calcination temperature 600°C and 26,64 nm with 35% size distribution at calcination temperature 800°C. SEM - EDS analysis showed that there are elemen tof O, Fe, Ni, and Cu which indicates the formation of Ni0,6Cu0,4Fe2O4 compound. Analysis using gas chromatography showed that Ni0,6Cu0,4Fe2O4 catalyst with calcination temperature of 600oC and reaction temperature of 200°C and 300°C has the highest activity of the conversion CO2/H2 to ethanol at 0.1992% and 0.2752% yield. Keyword: nanocatalys, sol-gel method, conversion CO2/H2, pectin, alcohol.

Jenis Karya Akhir:	Skripsi
Subyek:	> Q Science (General)
Program Studi:	FAKULTAS MIPA > Prodi Kimia
Pengguna Deposit:	5803272 . Digilib
Date Deposited:	21 Dec 2016 03:58
Terakhir diubah:	21 Dec 2016 03:58
URI:	http://digilib.unila.ac.id/id/eprint/24715

Actions (login required)

Lihat Karya Akhir