SINTESIS DAN KARAKTERISASI NANOKATALIS Ni(1-x)VxFe2O4 SEBAGAI FOTOKATALIS PADA FOTODEGRADASI ZAT WARNA REMAZOL GOLDEN YELLOW

ROMIYATI , 1427011010 (2016) SINTESIS DAN KARAKTERISASI NANOKATALIS Ni(1-x)VxFe2O4 SEBAGAI FOTOKATALIS PADA FOTODEGRADASI ZAT WARNA REMAZOL GOLDEN YELLOW. Masters thesis, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK (ABSTRACT).pdf Download (32Kb) | Preview
Preview	File PDF TESIS TANPA BAB PEMBAHASAN.pdf Download (1664Kb) | Preview
	File PDF TESIS FULL.pdf Restricted to Hanya pengguna terdaftar Download (2304Kb)

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

ABSTRAK Pada penelitian ini, nanokatalis Ni(1-x)VxFe2O4 dibuat dengan menggunakan metode sol - gel. Persiapan katalis dilakukan dengan melarutkan garam nitrat dari besi dan nikel, dan amonium vanadat dalam larutan pektin dan kemudian campuran diaduk secara menyeluruh dengan menggunakan pengaduk magnetik sampai pH 11 dan kemudian diproses beku keringkan. Sampel kering dikalsinasi pada suhu 600 dan 800oC, kemudian diuji dan karakterisasi dengan menggunakan teknik beberapa tehnik. Hasil karakterisasi XRD menunjukkan bahwa bahan terdiri dari fasa kristal mayoritas spinel Ni(1-x)VxFe2O4. Perhitungan ukuran kristal menggunakan persamaan Scherrer, membuktikan bahwa ukurannya adalah 34,61 nm untuk katalis dikalsinasi pada 600oC dan 47,84 nm untuk katalis dikalsinasi pada 800oC, analisis TEM membuktikan bahwa ukuran butir spinel ini berada di kisaran 27,02 nm untuk katalis dikalsinasi pada 600oC dan 55,37 nm untuk katalis dikalsinasi pada 800oC. Analisis FTIR menunjukkan bahwa situs asam yang dominan adalah asam Lewis, dan analisis PSA menunjukkan distribusi ukuran partikel katalis kurang dari 20%. Percobaan fotodegradasi dilakukan dengan menggunakan lampu UV dan radiasi sinar matahari, dan kinerjanya dievaluasi dengan mengukur absorbansi pada 407 nm menggunakan spektrometer UV-Vis. Hasil eksperimen menunjukkan bahwa katalis Ni0,5V0,5Fe2O4 yang dikalsinasi pada 600oC dan katalis Ni0,9V0,1Fe2O4 yang dikalsinasi pada 800oC masingmasing menunjukkan bahwa konsentrasi remazol golden yellow berkurang menjadi 14 dan 20% menggunakan radiasi sinar matahari, 36 dan 43% menggunakan radiasi UV. Keyword: Nanokatalis, pektin, fotodegradasi, remazol golden yellow ABSTRACT In this study, Ni(1-x)VxFe2O4 nanocatalyst has been prepared using a sol – gel method. The catalyst was prepared by dissolving nitrate salts of iron and nickel, and ammonium vanadate in pectin solution and then the mixture was stirred thoroughly using magnetic stirrer while adjusting pH to 11, and finally subjected to freeze – drying process. Dried sample was calcined at 600 and 800oC, and then tested and characterized using several techniques. The results of XRD characterization indicated that material consists of a majority crystalline phase of spinel Ni(1-x)VXFe2O4 . Crystalite size calculation using Scherrer equation, proved that the size is 34.61 nm for the catalyst calcined at 600oC and 47.84 nm for the catalyst calcined at 800oC, TEM analysis revealed hat the grain size of this spinel is aproximately 27.02 nm for the catalyst calcined at 600oC and 55.37 nm for the catalyst calcined at 800oC. FTIR analysis implied that the prominent acid sites is Lewis acid, and PSA analysis showed that the particle witn nanao-size is less than 20%. Photodegradation experiments were conducted using UV lamp and sunlight irradiation, and its performance was evaluated by measuring the absorbance at 407 nm using UV-Vis spectrometer. The experimental results using catalyst Ni0.5V0.5Fe2O4 calcined at 600 oC and catalyst Ni0.9V0.1Fe2O4 calcined at 800 oC, respectively, demonstrated that the concentration of the remazol golden yellow was reduced to 14 and 20% using sunlight irradiation and into 36 and 43% using UV irradiation. Keyword: Nanocatalyst, pectin, photodegradation, remazol golden yellow

Jenis Karya Akhir:	Tesis (Masters)
Subyek:	> QD Chemistry
Program Studi:	FAKULTAS MIPA > Prodi Magister Ilmu Kimia
Pengguna Deposit:	3654009 . Digilib
Date Deposited:	23 Dec 2016 01:53
Terakhir diubah:	23 Dec 2016 01:53
URI:	http://digilib.unila.ac.id/id/eprint/24837

Actions (login required)

Lihat Karya Akhir