SINTESIS DAN KARAKTERISASI NANOTITANIA YANG DIDOPING FLUOR MENGGUNAKAN METODE SOL-GEL

LAURA MEGADIA SARI, (1427041004) (2017) SINTESIS DAN KARAKTERISASI NANOTITANIA YANG DIDOPING FLUOR MENGGUNAKAN METODE SOL-GEL. Masters thesis, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK (ABSTRACT).pdf Download (23Kb) | Preview
	File PDF TESIS FULL.pdf Restricted to Hanya pengguna terdaftar Download (2005Kb)
Preview	File PDF TESIS TANPA BAB PEMBAHASAN.pdf Download (2006Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Telah dilakukan sintesis dan karakterisasi nanotitania menggunakan metode solgel. Sebagai sumber titania digunakan titanium tetraisopropoxide (TTIP) dan isoprophyl alcohol sebagai pelarut. Dalam mensintesis digunakan tween-80 sebagai surfaktan dan NH4F sebagai sumber doping fluor (F). Jumlah sampel yang disintesis sebanyak satu sampel nanotitania murni dan empat sampel F-TiO2 dengan variasi doping F masing-masing 0,4 g; 0,6 g; 0,8 g dan 1 g. Sampel dikalsinasi pada suhu 500 ℃ selama 4 jam. Seluruh sampel berbentuk bubuk dan dikarakterisasi menggunakan X-Ray Diffraction (XRD), Transmission Electron Microscope (TEM), Ultra Violet Visible (UV-Vis) Spectroscopy dan uji aktivitas katalitik pada larutan fenol 100 ppm. Hasil uji XRD menunjukkan bahwa sampel nanotitania dan F-TiO2 memiliki fasa murni anatase dengan ukuran partikel masing-masing sebesar 16,8 nm dan 23,8 nm. Penambahan doping F dipandang dapat meningkatkan kristalinitas nanotitania. Hasil uji TEM didapatkan ukuran partikel nanotitania 22,6 nm dan 21,1 nm untuk F-TiO2. Hasil uji aktivitas katalis menunjukkan bahwa dengan penambahan doping F pada nanotitania mengakibatkan kemampuan fotokatalitik nanotitania mengalami peningkatan di bawah sinar matahari (visible light). Kata kunci: Fenol, metode sol-gel, NH4F, titania, uji aktivitas katalis. ABSTRACT The synthesis and characterization of nanotitania has been carried out by sol-gel method. Titanium tetraisopropoxide (TTIP) used as a source of titania and isoprophyl alcohol as a solvent. In the synthesis, tween-80 was added as a surfactant and as a source of fluor (F) doping was used NH4F with variation of 0,4; 0,6; 0,8 and 1 gram. Samples were calcined at 500 ℃ for 4 hours. The whole sample were characterized using X-Ray Diffraction (XRD), Transmission Electron Microscope (TEM), Ultra Violet Visible (UV-Vis) spectroscopy and test catalytic activity at 100 ppm phenol solution. XRD test results showed that the samples nanotitania and F- TiO2 has a pure anatase phase with particle sizes of 16.8 nm and 23.8 nm. The addition of F doping can improve the crystallinity of nanotitania. TEM results showed that particle size of 22.6 nm for nanotitania and 21.1 nm for F-TiO2. The results of the catalyst activity test showed that the addition of F doping on nanotitania enhanced photocatalytic ability of nanotitania in sunlight (visible light). Keywords: Catalyst activity test, NH4F, phenol, sol-gel method, titania.

Jenis Karya Akhir:	Tesis (Masters)
Subyek:	> QC Physics
Program Studi:	FAKULTAS MIPA > Prodi Magister Ilmu Fisika
Pengguna Deposit:	8069612 . Digilib
Date Deposited:	31 Jan 2017 03:08
Terakhir diubah:	31 Jan 2017 03:08
URI:	http://digilib.unila.ac.id/id/eprint/25360

Actions (login required)

Lihat Karya Akhir