PENGARUH PENAMBAHAN MAGNESIUM OKSIDA (0, 20, 25, dan 30 wt%) TERHADAP KARAKTERISTIK TERMAL DAN KONDUKTIVITAS TERMAL KERAMIK CORDIERITE BERBASIS SILIKA SEKAM PADI

Juniati Br Simbolon, (1217041026) (2017) PENGARUH PENAMBAHAN MAGNESIUM OKSIDA (0, 20, 25, dan 30 wt%) TERHADAP KARAKTERISTIK TERMAL DAN KONDUKTIVITAS TERMAL KERAMIK CORDIERITE BERBASIS SILIKA SEKAM PADI. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

[img]
Preview
Text
ABSTRAK (ABSTRACT).pdf

Download (8Kb) | Preview
[img] Text
SKRIPSI FULL.pdf
Restricted to Registered users only

Download (1067Kb)
[img]
Preview
Text
SKRIPSI FULL TANPA BAB PEMBAHASAN.pdf

Download (569Kb) | Preview

Abstrak

ABSTRAK Telah dilakukan sintesis dan karakterisasi cordierite berbasis silica sekam padi dengan penambahan magnesium oksida 0, 20, 25, dan 30%wt. Cordierite disintesis dengan menggunakan silica dari sekam padi yang diperoleh dengan metode sol gel, Al2O3 dan magnesium oksida dengan menggunakan metode padatan yang kemudian disinterring pada suhu 1250ºC dengan waktu tahan selama 3 jam. Dari penambahan magnesium Oksida pada cordierite menghasilkan nilai konduktivitas termal sebesar 2,90-3,98 (W/mK). Penambahan paduan MgO ini juga mengakibatkan penurunan nilai densitas dan peningkatan nilai porositas sampel cordierite serta menurunnya nilai penyusutan. Kata Kunci.Cordierite, DTA-TGA, Konduktivitastermal, Magnesium oksida, Silika sekam padi ABSTRACT In this study, the effect of magnesium oxide addition on thermal characteristics and thermal conductivity of cordierite synthesized from rice husk silica was investigated by addition of magnesium oxide of 0, 20, 25, and 30%wt. The samples were subjected to sintering treatment at a temperature of 1250ºC with a holding time of 3 hours. The addition of magnesium oxide in the cordierite was found to increase thermal conductivity in the range of 2.91 to 3.16 (W / m.K), decrease density, increase the porosity cordierite, and decline the shrinkage.

Tipe Karya Ilmiah: Skripsi
Subyek: Q Science (General)
Q Science (General) > QC Physics
Program Studi: Fakultas MIPA > Prodi Fisika
Depositing User: 8587282 . Digilib
Date Deposited: 24 Feb 2017 06:15
Last Modified: 24 Feb 2017 06:15
URI: http://digilib.unila.ac.id/id/eprint/25712

Actions (login required)

View Item View Item