EKSTRAKSI DAN DEALUMINASI SILIKA DARI ABU AMPAS TEBU (Bagasse ash) DENGAN PERLAKUAN ASAM NITRAT SEBAGAI PREKURSOR UTAMA SINTESIS ZEOLIT ZSM-5

FATIMAH, 1317011022 (2017) EKSTRAKSI DAN DEALUMINASI SILIKA DARI ABU AMPAS TEBU (Bagasse ash) DENGAN PERLAKUAN ASAM NITRAT SEBAGAI PREKURSOR UTAMA SINTESIS ZEOLIT ZSM-5. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG .

Preview	File PDF ABSTRAK.pdf Download (302Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya pengguna terdaftar Download (3507Kb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (2757Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

ABSTRAK Telah dilakukan penelitian tentang ekstraksi dan dealuminasi silika dari abu ampas tebu (SCBA) menggunakan asam nitrat dan selanjutnya digunakan sebagai prekursor utama dalam sintesis Zeolite Secony Mobile-5 (ZSM-5). Silika yang diperoleh dari hasil ekstraksi dan dealuminasi dikarakterisasi dengan spektrofotometer infra merah (IR), X-Ray diffraction (XRD), dan X-Ray Fluorescence (XRF). Hasil karakterisasi menunjukkan adanya kandungan silika ditandai dengan adanya gugus siloksan dalam sampel yang ditunjukkan pada panjang gelombang 1078 cm -1 dan silika yang diperoleh berbentuk amorf, serta rasio Si/Al dalam silika sebesar 4,63. Rasio Si/Al dalam silika masih rendah maka pada silika dilakukan proses dealuminasi menggunakan asam nitrat dengan berbagai variasi konsentrasi dan didapat konsentrasi optimum yakni HNO 2 M dengan rasio Si/Al sebesar 51,37. Silika yang diperoleh dari proses dealuminasi dengan HNO 2 M digunakan sebagai sumber silika dalam mensintesis zeolit ZSM-5. Zeolit ZSM-5 telah berhasil disintesis dari silika baggase ash yang telah didealuminasi, kemudian zeolit yang diperoleh dikarakterisasi. Hasil karakterisasi menunjukkan puncak yang tidak jauh berbeda dengan zeolit ZSM-5 hasil sintesis dari silika komersil dan zeolit ZSM-5 standar puncaknya yaitu 2θ= 7,9; 8,05; dan 3 23,26˚. Rasio Si/Al sebesar 15,18 termasuk rasio yang cukup tinggi. Karakterisasi Scanning Electron Microscopy (SEM) diperoleh morfologi yang tidak jauh berbeda antara kedua sampel. Zeolit ZSM-5 dari silika komersil memiliki tingkat kristalinitas yang lebih tinggi dari pada zeolit dari silika baggase ash yang masih mengandung fasa amorf didalamnya. Kata Kunci : Ampas tebu (baggase), Silika, Zeolit, Zeolit ZSM-5, Dealuminasi, Asam Nitrat. ABSTRACT It has been carried out the research of extraction and dealumination of silica from sugarcane bagasse ash (SCBA) with nitric acid and then used as the main precursor in synthesizing of Zeolite Secony Mobile-5 (ZSM-5). Silica obtained from the extraction and dealumination was characterized by an infrared spectrophotometer (IR), X-Ray diffraction (XRD), and X-Ray fluorescence (XRF). The results showed the presence of silica indicated the existency of siloxane groups in the sample at wavelength 1078 cm -1 and the amorphous silica has obtained with Si/Al ratio 4.63. Si/Al ratio is still low in silica, then silica was performed dealumination process with nitric acid in various concentrations and obtained the optimum concentration of HNO 2 M with Si/Al ratio 51.37. The result of silica from dealumination process with HNO 3 2 M was used as a silica source in synthesis of ZSM-5 zeolite. ZSM-5 zeolite was synthesized succesfully from dealumination of silica baggase ash, and then zeolite produced characterized. The result of characterization showed that the peaks are not too different from ZSM-5 zeolite synthesized from commercial silica and zeolite ZSM-5 standard having peak at 2θ = 7.9; 8.05; and 23.26˚. Si/Al ratio at 15.18 is a high enough ratio. The result of characterization scanning electron microscopy (SEM) obtained morphology that is not much different between the two samples. ZSM-5 zeolite from a commercial silica has a higher degree of crystallinity than the zeolite of silica baggase ash still containing an amorphous phase. Keywords: Bagasse (baggase), silica, zeolite, zeolite ZSM-5, dealumination, Nitrit Acid.

Jenis Karya Akhir:	Skripsi
Subyek:	> Q Science (General)
Program Studi:	FAKULTAS MIPA > Prodi Kimia
Pengguna Deposit:	18090176 . Digilib
Date Deposited:	22 Jul 2017 03:29
Terakhir diubah:	22 Jul 2017 03:29
URI:	http://digilib.unila.ac.id/id/eprint/27367