SINTESIS ZSM-5 (Zeolite Secony Mobile-5) DARI SILIKA ABU AMPAS TEBU (Bagasse Ash) MENGGUNAKAN METODE HIDROTERMAL

ANGGI WIDIAWATI, 1317011084 (2017) SINTESIS ZSM-5 (Zeolite Secony Mobile-5) DARI SILIKA ABU AMPAS TEBU (Bagasse Ash) MENGGUNAKAN METODE HIDROTERMAL. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM , UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK.pdf Download (12Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya pengguna terdaftar Download (3323Kb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (2750Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

ABSTRAK Pada penelitian ini telah dilakukan sintesis ZSM-5 (Zeolite Secony Mobile-5) dari silika abu ampas tebu (bagasse ash) menggunakan metode hidrotermal. Silika abu ampas tebu diperoleh dari ekstraksi dengan metode alkali (NaOH), yang selanjutnya digunakan sebagai sumber silika dalam mensintesis zeolit. Hasil karakterisasi X-Ray Fluorosence (XRF) menunjukkan bahwa silika abu ampas tebu memiliki rendemen sebesar 10% dengan nilai rasio Si/Al 4,631, hasil Fourier Transform Infrared (FTIR) menunjukkan adanya gugus Si-O-Si dan Si-OH dalam silika abu ampas tebu, serta hasil X-Ray Diffraction (XRD) menunjukkan silika abu ampas tebu bersifat amorf. ZSM-5 dari silika abu ampas tebu disintesis dengan variasi suhu, waktu, penambahan template TPA-Br, dan penambahan benih zeolit ZSM-5. Hasil karakterisasi XRD pada zeolit menunjukkan bahwa ZSM-5 berhasil disintesis dari silika abu ampas tebu yang ditunjukkan dengan adanya puncak yang muncul sekitar 2θ = 7, 8, 9, 23, dan 24° tanpa adanya penambahan template TPA-Br dan benih zeolit ZSM-5. ZSM-5 dengan tingkat kristalinitas yang baik diperoleh pada sintesis dengan menggunakan suhu 170°C selama 96 jam. Berdasarkan hasil XRF diperoleh rasio Si/Al zeolit dari silika abu ampas tebu yaitu 5,89, dan karakterisasi Scanning Electron Microscope (SEM) menunjukkan bahwa morfologi kristal ZSM-5 berbentuk segi enam meskipun masih ada yang belum sempurna. Jadi dapat disimpulkan bahwa pada penelitian ini berhasil mensintesis ZSM-5 dari silika abu ampas tebu. Kata kunci: ampas tebu, abu ampas tebu, ekstraksi, silika abu ampas tebu, zeolit ZSM-5, hidrotermal. ABSTRACT It has been carried out the research of the synthesize Zeolite Secony Mobile-5 (ZSM-5) from Sugarcane Bagasse Ash (SCBA) silica using hydrothermal method. Bagasse ash silica is obtained from extraction by alkali method (NaOH), which is then used as a source of silica in synthesizing zeolite. The results of X-Ray Fluorosence (XRF) characterization showed that bagasse ash silica has 10% of a yield with a value of Si/Al ratio 4,631, the characterization of Fourier Transform Infrared (FTIR) showed the presence of Si-O-Si and Si-OH group in bagasse ash silica, and the characterization of X-Ray Diffraction (XRD) showed that silica from Sugarcane Bagasse Ash are amorphous phase. ZSM-5 from bagasse ash silica is synthesized with variation of temperature, time, use of TPA-Br template, and addition seed of ZSM-5. The results of characterization XRD zeolite showed that ZSM-5 was successfully synthesized from bagasse ash silica as shown in the presence of peak that appeared about 2θ = 7, 8, 9, 23, and 24° without the addition of TPA-Br template and ZSM-5 seed. ZSM-5 with a good degree of crystallinity was obtained in synthesis using a temperature of 170°C for 96 hours. Based on the result of caracterization XRF, the ratio of Si/Al zeolite from silica bagasse ash was 5,89, and the caracterization of Scanning Electron Microscope (SEM) showed that the ZSM-5 crystal morphology is hexagon-shaped although there is still not yet perfect. So it can be concluded that the ZSM-5 from bagasse ash silica was successfully synthesized. Keyword: bagasse, bagasse ash, extraction, bagasse ash silica, ZSM-5 zeolite, hydrothermal.

Jenis Karya Akhir:	Skripsi
Subyek:	> QD Chemistry
Program Studi:	FAKULTAS MIPA > Prodi Kimia
Pengguna Deposit:	57396900 . Digilib
Date Deposited:	07 Aug 2017 07:53
Terakhir diubah:	07 Aug 2017 07:53
URI:	http://digilib.unila.ac.id/id/eprint/27778

Actions (login required)

Lihat Karya Akhir