UJI AKTIVITAS KATALIS NANOKOMPOSIT Ni0,5Cu0,5Fe2O4 DALAM MENGKONVERSI NANOSELULOSA MENJADI GULA ALKOHOL YANG DIIRADIASI SINAR UV

RENITA SUSANTI , 1317011059 (2017) UJI AKTIVITAS KATALIS NANOKOMPOSIT Ni0,5Cu0,5Fe2O4 DALAM MENGKONVERSI NANOSELULOSA MENJADI GULA ALKOHOL YANG DIIRADIASI SINAR UV. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM , UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK.pdf Download (60Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya pengguna terdaftar Download (1117Kb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (1118Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Penelitian ini bertujuan untuk mengetahui aktivitas katalis nanokomposit Ni0,5Cu0,5Fe2O4 dalam konversi nanoselulosa menjadi gula alkohol. Nanokatalis Ni0,5Cu0,5Fe2O4 dipreparasi menggunakan metode sol-gel dengan pektin sebagai agen pengemulsi dan dikalsinasi pada temperatur 600oC. Uji aktivitas katalis dilakukan melalui konversi nanoselulosa menjadi gula alkohol dengan bantuan radiasi sinar UV pada variasi waktu penyinaran 30, 45, dan 60 menit. Karakterisasi dengan XRD menunjukkan terbentuknya nanokatalis Ni0,5Cu0,5Fe2O4 dengan adanya fasa CuFe2O4, NiFe2O4 yang saling bertumpang tindih. Ukuran rata-rata partikel dihitung dengan persamaan Scherrer sebesar 14,9 nm. Analisis keasaman dengan metode gravimetri menunjukkan bahwa katalis memiliki keasaman 1,931 mmol piridin/g katalis. Analisis dengan FTIR membuktikan bahwa situs asam Lewis merupakan situs asam yang dominan ditunjukkan oleh serapan pada bilangan gelombang 1591,27 cm-1. Hasil analisis morfologi katalis dengan metode TEM menunjukkan katalis memiliki ukuran rata-rata sebesar 18,9 nm dengan morfologi yang cukup terdistribusi secara merata meski masih terdapat aglomerasi. Analisis menggunakan KCKT mengungkapkan bahwa katalis mampu mengkonversi nanoselulosa menjadi sorbitol dengan hasil tertinggi diperoleh pada waktu radiasi 60 menit sebesar 4,6 %. Kata kunci: nanokatalis, pektin, nanoselulosa, gula alkohol, sinar UV. abstract The purpose of this research was obtain, to know the catalytic activity of Ni0.5Cu0.5Fe2O4 nanocomposite in converting nanocellulose into alcohol sugar. Nanocatalyst Ni0.5Cu0.5Fe2O4 was prepared using sol-gel method with pectin as an emulsifying agent and calcined at the temperature 600°C. It’s activity test was carried out through conversion of nanoselulose to alcohol sugar irradiated by UV light with the irradiation time 30, 45, and 60 minutes. Characterization with XRD technique indicated the presence of CuFe2O4 and NiFe2O4 as a major phase which are superimposed confirming the formation of Ni0.5Cu0.5Fe2O4. The average particle size calculated by Scherrer method is 14.9 nm. The acidity analysis by the gravimetric method revealed that the acidity of nanocatalyst is 1.931 mmol pyridine / g catalyst. FTIR analysis proved that Lewis acid sites is the dominan site shown on wave number of 1591.27 cm-1. The result of catalyst morphology analysis using TEM method showed that the catalyst has average size of 18.9 nm with fairly distributed morphology evenly although there is still agglomeration. Analysis using HPLC revealed that the catalyst was able to convert nanocellulose into sorbitol with the highest yield of 4.6% obtained at 60 minutes of radiation. Keyword: nanocatalyst, pectin, nanocellulose, alcohol sugar, UV light

Jenis Karya Akhir:	Skripsi
Subyek:	> QD Chemistry
Program Studi:	FAKULTAS MIPA > Prodi Kimia
Pengguna Deposit:	77751631 . Digilib
Date Deposited:	24 Oct 2017 02:13
Terakhir diubah:	24 Oct 2017 02:13
URI:	http://digilib.unila.ac.id/id/eprint/28777

Actions (login required)

Lihat Karya Akhir