KONVERSI NANOSELULOSA MENJADI GULA ALKOHOL MENGGUNAKAN NANOKOMPOSIT Ni0,3Cu0,7Fe2O4 YANG DIIRADIASI SINAR UV

Mega Mawarti, 1347011005 (2017) KONVERSI NANOSELULOSA MENJADI GULA ALKOHOL MENGGUNAKAN NANOKOMPOSIT Ni0,3Cu0,7Fe2O4 YANG DIIRADIASI SINAR UV. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK.pdf Download (9Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya pengguna terdaftar Download (910Kb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (725Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Telah dilakukan preparasi nanokomposit Ni0,3Cu0,7Fe2O4 menggunakan metode sol-gel dan pektin sebagai agen pengemulsi dan dikalsinasi pada temperatur 600oC, dilanjutkan dengan uji aktivitas fotokatalitik. Katalis telah dikarakterisasi menggunakan peralatan XRD, FTIR, dan TEM. Selanjutnya katalis yang diperoleh digunakan untuk uji konversi nanoselulosa menjadi gula alkohol yang diiradiasi dengan sinar UV pada variasi waktu penyinaran 30 menit, 45 menit, dan 60 menit. Hasil analisis difraksi sinar-X (XRD) terhadap katalis Ni0,3Cu0,7Fe2O4 menunjukkan adanya beberapa fasa kristal yakni fasa mayor CuFe2O4 dan NiFe2O4, serta fasa minor Fe3O4, CuO dan NiO. Hasil analisis keasaman katalis dengan metode gravimetri sebesar 1,606 mmol piridin/g katalis. Berdasarkan metode Fourier Transform Infra Red (FTIR) memberikan hasil jenis situs asam Lewis yang lebih dominan dari situs asam Bronsted-Lowry. Hasil analisis morfologi katalis dengan metode Transmission Electron Microscopy (TEM) menunjukkan fasa kristalin yang terbentuk terdistribusi secara merata (homogen) dan masih terdapat sedikit aglomerasi dengan ukuran butiran rata-rata sebesar 19,31 nm. Analisis menggunakan Kromatografi Cair Kinerja Tinggi (KCKT) mengungkapkan bahwa nanoselulosa yang telah dikonversi menjadi sorbitol dan manitol pada waktu penyinaran 60 menit memberikan konsentrasi sorbitol lebih besar dibandingkan manitol, yakni 1348 ppm. Kata kunci: nanoselulosa, gula alkohol, sinar UV, pektin ABSTRACT Ni0.3Cu0.7Fe2O4 nanocomposite was prepared using sol-gel method and pectin as an emulsifying agent and calcined at 600oC, followed by photocatalytic activity test. Then, catalyst was characterized by different techniques, such as XRD, FTIR, and TEM. After characterization, catalyst was used to convert nanocellulose into alcohol sugar by UV-light irradiation at variation of time 30 minutes, 45 minutes and 60 minutes. The result of X-ray diffraction (XRD) analysis of Ni0.3Cu0.7Fe2O4 catalyst showed there are several crystallite phases of CuFe2O4 and NiFe2O4 as major phases and Fe3O4, CuO and NiO as minor phases. The result of acidity property analyzed by gravimetric method was 1.606 mmol pyridine/g catalyst. According to Fourier Transform Infra Red (FTIR), resulted that Lewis acid sites are more dominant than Bronsted-Lowry sites. The results of morphological analysis of catalyst using Transmission Electron Microscopy (TEM) showed that the crystalline phases was distributed evenly (homogeneous) and there was still a slight agglomeration with an average size of 19.31 nm. Analysis using High Performance Liquid Chromatography (HPLC) revealed that nanocellulose was converted into sorbitol and mannitol at 60 minutes retention time with the sorbitol product as the highest concentration, which was 1348 ppm. Keywords: alcohol sugar, uv-light, nanocellulose, pectin

Jenis Karya Akhir:	Skripsi
Subyek:	> Q Science (General)
Program Studi:	FAKULTAS MIPA > Prodi Kimia
Pengguna Deposit:	00270567 . Digilib
Date Deposited:	24 Oct 2017 03:15
Terakhir diubah:	24 Oct 2017 03:15
URI:	http://digilib.unila.ac.id/id/eprint/28778

Actions (login required)

Lihat Karya Akhir