PENGOLAHAN CPO PARIT MENJADI LIQUID FUEL DENGAN METODE PIROLISIS MENGGUNAKAN ZEOLIT SINTETIK BERBASIS SILIKA SEKAM PADI

MUHAMMAD YUSRY AHMADHANI , 1117011038 (2018) PENGOLAHAN CPO PARIT MENJADI LIQUID FUEL DENGAN METODE PIROLISIS MENGGUNAKAN ZEOLIT SINTETIK BERBASIS SILIKA SEKAM PADI. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRACT (ABSTRAK).pdf Download (120Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya pengguna terdaftar Download (4Mb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (4Mb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Dalam penelitian ini telah dilakukan sintesis zeolit-Y dari aluminium dan silika sekam padi menggunakan metode sol-gel. Zeolit-Y dikalsinasi pada suhu 600, 700, 800, dan 900 oC. Uji perengkahan dilakukan pada minyak CPO parit, bagas tebu, serta campuran bagas tebu dan minyak CPO parit. Campuran bagas tebu dan minyak CPO parit menggunakan zeolit-Y yang dikalsinasi dengan suhu 600, 700, 800 oC memiliki kondisi optimum dengan rendemen liquid fuel sebesar 35,23%; 31,60%; dan 26,47%. Hasil GC-MS menunjukkan bahwa hasil uji perengkahan pada campuran bagas tebu dan minyak CPO parit menggunakan zeolit-Y yang dikalsinasi pada suhu 700 °C memiliki kandungan hidrokarbon terbesar yaitu 85,54% dengan viskositas 2,9 cSt, densitas 0,861 g/mL, serta titik nyala sebesar 50oC. Katalis yang dikarakterisasi menggunakan XRD menunjukkan bahwa katalis zeolit-Y 600, 700, 800, dan 900 oC membentuk fasa nepheline, nephelite, maupun jadeite. Hasil analisis SEM menunjukkan bahwa pori dipermukaan zeolit berkurang ketika suhu kalsinasi meningkat. Karakterisasi dengan PSA menunjukkan distribusi ukuran partikel pada zeolit-Y 600, 700, dan 800 oC berturut-turut sebesar 92,1 nm, 294 nm, dan 336 nm. Hasil karakterisasi FTIR menunjukkan bahwa zeolit-Y 600, 700, 800, dan 900 oC merupakan situs asam BrØnsted-Lowry. Kata kunci : bagas tebu, liquid fuel, minyak CPO parit, reaksi perengkahan, zeolit-Y ABSTARCT The synthesized of zeolite-Y in this research had been done from aluminum and silica from rice husk using sol-gel method. Zeolite-Y calcined on temperature 600, 700, 800, and 900 0C. Cracking test was done on CPO waste, bagasse of sugarcane, and the mixture from bagasse of sugarcane and CPO waste. The mixture from bagasse of sugarcane and CPO waste used Zeolite-Y which was calcined on temperature 600, 700, 800 0C had optimum condition with liquid fuel yield 35,23%, 31,60%, and 26,47%. The result of GC-MS showed that cracking test on the mixture from bagasse of sugarcane and CPO waste used Zeolite-Y which was calcined on temperature 700 0C contained biggest hydrocarbon, it was 85,54% with the value of viscosity 2,9 cSt, density 0,861 g/mL, and flash point on 50 0C. Catalyst characterized by XRD showed that Zeolite-Y catalyst 600, 700, 800, and 900 0C forming nepheline, nephelite, or jadeite phase. The result of SEM analysis showed that the pores on the surface of zeolite reduced when the temperature of calcination was increased. PSA characterization showed that the distribution of particle size on Zeolite-Y 600, 700, 800, and 900 0C was Bronsted- Lowry’s acid site. Keyword: CPO waste soil, cracking reaction, liquid fuel, sugarcane bagasse, Zeolite-Y

Jenis Karya Akhir:	Skripsi
Subyek:	> Q Science (General)
Program Studi:	FAKULTAS MIPA > Prodi Kimia
Pengguna Deposit:	19501168 . Digilib
Date Deposited:	23 Feb 2018 02:34
Terakhir diubah:	23 Feb 2018 02:34
URI:	http://digilib.unila.ac.id/id/eprint/30523

Actions (login required)

Lihat Karya Akhir