PENGARUH KONSENTRASI EKSTRAK KULIT BUAH MAJA (AEGLE MARMELOS (L.) COREA) TERHADAP LAJU KOROSI BAJA KARBON API 5L PADA MEDIUM NaCl 3% DAN H2SO4 3%

AMILIA RASITIANI, 1417041009 (2018) PENGARUH KONSENTRASI EKSTRAK KULIT BUAH MAJA (AEGLE MARMELOS (L.) COREA) TERHADAP LAJU KOROSI BAJA KARBON API 5L PADA MEDIUM NaCl 3% DAN H2SO4 3%. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM , UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK.pdf Download (19Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya pengguna terdaftar Download (3730Kb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (2780Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Telah dilakukan penelitian mengenai pengaruh konsentrasi ekstrak kulit buah maja sebagai inhibitor pada baja karbon API 5L dalam medium korosif NaCl 3% dan H2SO4 3%. Perendaman baja karbon API 5L dilakukan selama 35 hari dengan variasi konsentrasi penambahan inhibitor ekstrak kulit buah maja 0%, 0,4%, 0,5%, 0,6%, 0,7%, dan 0,8%. Pengujian laju korosi dilakukan dengan metode kehilangan berat. Hasil penelitian menunjukkan laju korosi terbesar pada medium korosif NaCl 3% dan H2SO4 3% adalah pada konsentrasi inhibitor 0% , yaitu sebesar 0,06 x 104 mm/y dan 16,55 x 104 mm/y. Sementara, laju korosi terendah yaitu pada konsentrasi inhibitor 0,8% untuk medium korosif NaCl 3% dan 0,5% untuk medium korosif H2SO4 3%. Sehingga efektivitas korosi yang paling besar terjadi pada konsentrasi 0,8% pada medium korosif NaCl 3% dengan efektivitas sebesar 85,71%, dan 0,5% pada medium korosif H2SO4 3% dengan efektivitas sebesar 79,35%. Hasil karakterisasi X-Ray Diffraction (XRD) memperlihatkan bahwa fasa yang terbentuk adalah Fe murni. Karakterisasi Scanning Electron Microscopy (SEM) memperlihatkan cluster (gumpulan) tidak merata dan ukuran lebih kecil, lubang (hole) dan retakan (crack) juga lebih sedikit dengan inhibitor 0,8% untuk medium korosif NaCl 3% dan 0,5% untuk medium korosif H2SO4 3% dibandingkan dengan inhibitor 0% ekstrak kulit buah maja pada medium korosif NaCl 3% dan H2SO4 3%. Karakterisasi Energy Dispersive Spectroscopy (EDS) pada sampel dengan medium korosif H2SO4 3% didapatkan unsur S (Sulfat). Kata kunci: Baja karbon API 5L, ekstrak kulit buah maja, inhibitor korosi, NaCl, dan H2SO4. ASBTRACT A study has been conducted on the extract concentration effect of Maja Peel as an inhibitor of low carbon API 5L in corrosive medium of NaCl 3% and H2SO4 3%. The soaking process of low carbon API 5L was done for 35 days with variation of addition inhibitor concentrations at 0%, 0,4%, 0,5%, 0,6%, 0,7%, and 0,8%. The testing of Corrosion rate is done by weight loss method. The results showed that the highest corrosive rate in corrosive medium of NaCl 3% and H2SO4 3% was at 0% which is inhibitor concentration, 0,06 x 104 mm/y and 16,55 x 104 mm/y concentration. Meanwhile, the lowest corrosion rate at 0.8% inhibitor concentration for corrosive medium of NaCl 3% and 0.5% for H2SO4 3% corrosive medium. Hence, the greatest effectiveness of corrosion occurs at the concentration of 0.8% in a corrosive medium of NaCl 3% with effectiveness of 85,71% and 0.5% in corrosive medium of H2SO4 3% with the effectiveness of 79.35%. The characterization result of X-Ray Diffraction (XRD) shows that the phase formed is pure Fe. Characterization of Scanning Electron Microscopy (SEM) showed uneven clusters and smaller sizes, holes and cracks also with less than 0.8% inhibitors for corrosive medium of NaCl 3% and 0.5% for corrosive medium of H2SO4 3% compared with 0% inhibitor of maja peel extract on corrosive medium of NaCl 3% and H2SO4 3%. Characterization of Energy Dispersive Spectroscopy (EDS) in samples with corrosive medium of H2SO4 3% obtained the element S (Sulfate). Keywords: low carbon API 5L, the extract of maja peel, corrosion inhibitor, NaCl, and H2SO4.

Jenis Karya Akhir:	Skripsi
Subyek:	> QC Physics
Program Studi:	FAKULTAS MIPA > Prodi Fisika
Pengguna Deposit:	201899826 . Digilib
Date Deposited:	02 Jul 2018 03:01
Terakhir diubah:	02 Jul 2018 03:01
URI:	http://digilib.unila.ac.id/id/eprint/31909

Actions (login required)

Lihat Karya Akhir