SINTESIS DAN KARAKTERISASI BIOMASSA ALGA Spirulina sp. TERMODIFIKASI SILIKA-MAGNETIT SEBAGAI ADSORBEN ZAT WARNA KRISTAL VIOLET

ISMI ADITIYA, 1417011057 (2018) SINTESIS DAN KARAKTERISASI BIOMASSA ALGA Spirulina sp. TERMODIFIKASI SILIKA-MAGNETIT SEBAGAI ADSORBEN ZAT WARNA KRISTAL VIOLET. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

	File PDF ABSTRAK.pdf Download (11Kb)
	File PDF SKRIPSI FULL.pdf Restricted to Hanya pengguna terdaftar Download (1557Kb)
	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (1373Kb)

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Pada penelitian ini telah dilakukan sintesis hibrida alga Spirulina sp. dengan matriks silika (HAS) dan dimodifikasi dengan teknik pelapisan menggunakan partikel magnetit (Fe3O4) (HASM) untuk digunakan sebagai adsorben zat warna kristal violet dalam larutan. Karakterisasi material HAS dan HASM dengan spektrofotometer IR digunakan untuk mengetahui gugus fungsional, X-Ray Diffraction (XRD) digunakan untuk analisis tingkat kekristalan, dan Scanning Electron Microscopy With Energy Dispersive X-ray (SEM-EDX) untuk mengidentifikasi morfologi permukaan dan konstituen unsur. Hasil adsorpsi menunjukkan bahwa adsorpsi ini optimum dilakukan pada pH 8 dalam waktu 120 menit dengan konsentrasi kristal violet 400 mg/L dan dianalisis menggunakan spektrofotometer UV-Vis pada panjang gelombang maksimum kristal violet 591 nm. Kinetika adsorpsi kristal violet oleh HAS dan HASM cenderung mengikuti model kinetika pseudo orde dua dengan laju adsorpsi material HAS sebesar 0,0361 g mg-1 menit-1 dan HASM sebesar 0,0227 g mg-1 menit-1 dan model isoterm Freundlich dengan energi adsorpsi kurang dari 20,92 kJ mol-1 yang mengindikasikan adsorpsi terjadi secara fisika. Kata kunci : Biomassa alga Spirulina sp., magnetit, adsorpsi, kristal violet. ABSTRACT In this research, it has been conducted synthesis of Spirulina sp. algae hybrid with silica matrix (HAS) and modified by coating magnetite particles (Fe3O4) (HASM) to be used as adsorbent of crystal violet dye in the solution. Characterizations of HAS and HASM materials with infrared spectrophotometer (IR) were used to investigate a functional groups, X-Ray Diffraction (XRD) was used for analyzing of crystalline levels, and Scanning Electron Microscopy With Energy Dispersive X-ray (SEM-EDX) was conducted to identify the surface and elemental constituents of the materials. While, spectrophotometer of UV-Vis was used to analyze the maximum wavelength of crystal violet in solution. The result showed that the adsorpstion is optimum at pH 8 within 120 minutes with a concentration of crystal violet is 400 mg/L and at a maximum wavelength of crystal violet of 591 nm. Adsorption kinetics of crystal violet by HAS and HASM tend to follow pseudo second order kinetic model with the adsorption rate of HAS material of 0,0361 g mg-1 menit-1 and HASM material of 0,0227 g mg-1 menit-1 as well as Freundlich isotherm model with the energy of adsorption less than 20.92 kJ mol-1 indicating physical adsorption. Kata kunci : Spirulina sp. algae biomass, magnetite, adsorption, crystal violet.

Jenis Karya Akhir:	Skripsi
Subyek:	> Q Science (General)
Program Studi:	FAKULTAS MIPA > Prodi Kimia
Pengguna Deposit:	188236092 . Digilib
Date Deposited:	11 Oct 2018 07:42
Terakhir diubah:	11 Oct 2018 07:42
URI:	http://digilib.unila.ac.id/id/eprint/33605

Actions (login required)

Lihat Karya Akhir