STUDI PENAMBAHAN ASAP CAIR PELEPAH SAWIT SEBAGAI INHIBITOR KERAK CaCO3 DENGAN MENGGUNAKAN METODE SEEDED EXPERIMENT

WIDYA EKASARI, 1517011014 (2019) STUDI PENAMBAHAN ASAP CAIR PELEPAH SAWIT SEBAGAI INHIBITOR KERAK CaCO3 DENGAN MENGGUNAKAN METODE SEEDED EXPERIMENT. Fakultas Matematika dan Ilmu Pengetahuan Alam, UNIVERSITAS LAMPUNG.

Preview	File PDF 1. ABSTRAK.pdf Download (1952Kb) | Preview
	File PDF 2. SKRIPSI FULL.pdf Restricted to Hanya staf Download (3498Kb)
Preview	File PDF 3. SKRIPSI FULL TANPA BAB PEMBAHASAN.pdf Download (3407Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Terbentuknya kerak pada pipa merupakan masalah yang sering dijumpai pada industri diantaranya industri minyak, gas, dan kimia yang melibatkan proses desalinasi dan ketel. Salah satu kerak yang banyak dijumpai yaitu kalsium karbonat (CaCO3). Untuk mengatasi masalah tersebut, pada penelitian ini digunakan asap cair pelepah sawit sebagai inhibitor kerak CaCO3 yang ramah lingkungan menggunakan metode dengan penambahan bibit kristal (Seeded Experiment) pada suhu 90 oC. Larutan pertumbuhan CaCO3 yang digunakan yaitu 0,0250; 0,0375; 0,0500; dan 0,0625 M serta variasi inhibitor sebesar 5, 15, 25, dan 35%. Nilai persen efektivitas tertinggi terjadi pada konsentrasi 0,0250 M dengan penambahan inhibitor sebesar 35% yaitu sebesar 400%. Berdasarkan hasil Scanning Electron Microscopy (SEM) dan X-Ray Diffraction (XRD) menunjukkan kerak CaCO3 tanpa inhibitor terdiri dari kristal fasa kalsit, aragonit, dan sedikit vaterit, setelah penambahan inhibitor terdiri dari kristal fasa kalsit, vaterit, dan sedikit aragonit. Analisis kuantitatif menggunakan Particle Size Analyzer (PSA) menunjukan bahwa distribusi ukuran partikel kerak CaCO3 menjadi lebih kecil dengan adanya penambahan inhibitor berdasarkan nilai rata�rata (mean) yaitu dari 8,772 menjadi 6,331 μm dan nilai tengah (median) yaitu dari 8,187 menjadi 5,922 μm. Asap cair pelepah sawit terbukti dapat digunakan sebagai inhibitor untuk pertumbuhan kerak CaCO3 menggunakan metode seeded experiment. Kata kunci: Asap cair pelepah sawit, CaCO3, inhibitor, kerak The formation of scale on pipes is problem that is often encountered in industries including oil, gas, and chemical industries which involve desalination and boiler processes. One of scale that is often found is calcium carbonate (CaCO3). To overcome this problem, in this study it was used palm midrib liquid smoke as an environmentally friendly CaCO3 scale inhibitor using a method with the addition of seeds (seeded experiment) at temperature of 90 oC. CaCO3 growth solution used was 0.0250, 0.0375, 0.0500, dan 0.0625 M and inhibitor variations is 5, 15, 25, dan 35%. The highest percent value of inhibitor effectiveness occurs at concentration of 0.0250 M with addition of inhibitor of 35% that is equal to 400%. Based on the result of Scanning Electron Microscopy (SEM) and X-Ray Diffraction (XRD), it showed that CaCO3 scale without inhibitor consisted of crystal phase such as calcite, aragonite, and little vaterite, after the addition of inhibitor contains calcite, vaterite, and little aragonite. Quantitative analysis using Particle Size Analyzer (PSA) shows that CaCO3 scale particle size distribution becomes smaller with the addition of inhibitor based on the average value (mean) of 8.772 to 6.331 μm and the middle value (median) of 8.187 to 5.922 μm. Palm midrib liquid smoke is proven to be used as an inhibitor for the growth of CaCO3 scale using seeded experiment method. Keywords: palm midrib liquid smoke, CaCO3, inhibitor, scale

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika > 540 Kimia dan ilmu yang berhubungan
Program Studi:	FAKULTAS MIPA > Prodi Kimia
Pengguna Deposit:	UPT . Digilib2
Date Deposited:	29 Mar 2022 13:10
Terakhir diubah:	29 Mar 2022 13:10
URI:	http://digilib.unila.ac.id/id/eprint/56559

Actions (login required)

Lihat Karya Akhir