SINTESIS DAN KARAKTERISASI BASA SCHIFF DARI SALISILALDEHIDA DAN ETILENDIAMINA SEBAGAI SENSITIZER PADA DYE SENSITIZED SOLAR CELL (DSSC) BERBASIS SEMIKONDUKTOR ZnO DAN VARIASI ELEKTROLIT GEL

ANNISA TRI AGUSTIN, 1517011040 (2019) SINTESIS DAN KARAKTERISASI BASA SCHIFF DARI SALISILALDEHIDA DAN ETILENDIAMINA SEBAGAI SENSITIZER PADA DYE SENSITIZED SOLAR CELL (DSSC) BERBASIS SEMIKONDUKTOR ZnO DAN VARIASI ELEKTROLIT GEL. Fakultas Matematika dan Ilmu Pengetahuan Alam, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK.pdf Download (2380Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya staf Download (2379Kb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (2380Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Telah dilakukan sintesis senyawa basa Schiff dari salisilaldehida dan etilendiamina dengan metode kondensasi refluks. Basa Schiff hasil sintesis dikarakterisasi menggunakan spektrofotometri UV-Vis untuk menentukan serapan panjang gelombang, spektrofotometri IR untuk menentukan gugus fungsi, dan TG/DTA untuk analisis dekomposisi termal senyawa tersebut. Basa Schiff hasil sintesis kemudian diaplikasikan sebagai sensitizer pada Dye Sensitized Solar Cell (DSSC) menggunakan semikonduktor ZnO dan tiga variasi larutan elektrolit gel PEG 0,025 M; 0,05 M; dan 0,1 M untuk diukur kuat arus, tegangan, dan efisiensi kinerja DSSC. Hasil sintesis yang diperoleh yaitu kristal berwarna kuning cerah dengan rendemen sebesar 81,14%. Hasil karakterisasi menggunakan spektrofotometri UV-Vis menunjukkan bahwa basa Schiff mengalami pergeseran batokromik dari panjang gelombang senyawa pembentuknya 324 nm dan 328 nm ke panjang gelombang 335 nm dengan transisi n→π*. Data spektrum IR basa Schiff menunjukkan adanya serapan khas gugus azometina (-C=N-) pada bilangan gelombang 1610 cm-1 . Analisis dekomposisi termal menunjukan adanya kehilangan massa dari molekul air sebesar 10,2% pada rentang suhu 75-100 °C dan molekul basa Schiff sebesar 97,2% pada rentang suhu 180-300 °C. Hasil pengujian DSSC berbasis semikonduktor ZnO menggunakan larutan elektrolit gel PEG 0,1M menghasilkan kinerja paling baik dengan efisiensi sebesar 0,11% pada tegangan maksimum (Vmax) 234 mV serta kuat arus (Imax) 0,6 mA. Kata Kunci: basa Schiff, sensitizer, Dye Sensitized Solar Cell (DSSC), ZnO, elektrolit gel The Schiff base compound has been synthesized from salicylaldehyde and ethylenediamine with reflux condensation method. The synthesized Schiff base was characterized using UV-Vis spectrophotometry to determine the wavelength, IR spectrophotometry to determine functional groups, and TG/DTA for the analysis of the thermal decomposition of these compound. Then, the synthesized Schiff base was applied as a sensitizer in Dye Sensitized Solar Cell (DSSC) using a ZnO semiconductor and three variation of PEG gel electrolytes of 0.025 M; 0.05 M; and 0.1 M respectively. The synthesis of Schiff base obtained bright yellow crystal with a yield of 81.14%. The characterization results using UV-Vis spectrophotometry showed that the Schiff base had a batochromic shift from the wavelength of its constituent compounds 324 nm and 328 nm to 335 nm with the n→π* transition. Therefore, the IR spectrum data of Schiff base showed the typical absorption of azometine groups (-C=N-) at wave number 1610 cm-1 . Analysis of thermal decomposition showed a mass loss from a water molecule of 10.2% in the temperature range of 75-100 °C and a Schiff base molecule of 97.2% in the temperature range of 180-300 °C. Afterwards, the DSSC based ZnO semiconductor test results using a 0.1 M PEG gel electrolyte showed the best performance with an efficiency of 0.11% at a maximum voltage (Vmax) of 234 mV and a strong current (Imax) of 0.6 mA. Key word: Schiff base, sensitizer, Dye Sensitized Solar Cell (DSSC), ZnO, gel electrolyte

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika > 540 Kimia dan ilmu yang berhubungan
Program Studi:	FAKULTAS MIPA > Prodi Kimia
Pengguna Deposit:	UPT . Digilib2
Date Deposited:	29 Mar 2022 13:21
Terakhir diubah:	29 Mar 2022 13:21
URI:	http://digilib.unila.ac.id/id/eprint/56615

Actions (login required)

Lihat Karya Akhir