STUDI TRANSPOR FENOL MENGGUNAKAN METODE POLYMER INCLUSION MEMBRANE (PIM) DENGAN KOPOLI(EUGENOL-DIVINIL BENZENA) SEBAGAI SENYAWA CARRIER

DESSY TIARA ELVIA NITA SARI, 1417011022 (2019) STUDI TRANSPOR FENOL MENGGUNAKAN METODE POLYMER INCLUSION MEMBRANE (PIM) DENGAN KOPOLI(EUGENOL-DIVINIL BENZENA) SEBAGAI SENYAWA CARRIER. Fakultas Matematika dan Ilmu Pengetahuan Alam, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK.pdf Download (154Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya staf Download (1713Kb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (1713Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Fenol merupakan senyawa organik beracun, berbahaya dan sulit didegradasi yang banyak ditemukan sebagai polutan di perairan. Penelitian mengenai studi transpor fenol menggunakan metode Polymer Inclusion Membrane (PIM) dengan kopoli(eugenol-DVB) sebagai senyawa carrier dilakukan untuk mengatasi masalah tersebut. Beberapa parameter yang berpengaruh terhadap transpor fenol telah dilakukan diantaranya yaitu pH fenol fasa sumber, konsentrasi NaOH fasa penerima, ketebalan membran PIM dan waktu transpor. Sintesis kopoli(eugenol�DVB) dilakukan melalui reaksi kopolimerisasi antara eugenol dengan divinil benzena (DVB) 10 % menggunakan katalis BF3O(C2H5)2. Serbuk kopolimer yang dihasilkan dikarakterisasi menggunakan FT-IR. Konsentrasi fenol setelah transpor ditentukan dengan metode spektrofotometri UV-Vis menggunakan reagen 4-aminoantipirin dan absorbansinya diukur pada panjang gelombang λ=456 nm. Hasil penelitian menunjukkan bahwa membran PIM dengan senyawa carrier kopoli(eugenol-DVB) mampu mentranspor fenol secara efektif sebesar 89,40 % pada kondisi optimum: pH fenol fasa sumber 5,5, konsentrasi NaOH 0,1 M, ketebalan membran PIM tipe T27 dan waktu transpor selama 24 jam. Membran PIM yang telah digunakan untuk transpor selama 24 jam dikarakterisasi menggunakan SEM dan FT-IR Transpor fenol dengan logam kompetitor Cu(II) dan Pb(II) menghasilkan konsentrasi fenol yang tertranspor lebih kecil dibandingkan transpor tanpa logam yaitu sebesar 27,25 %. Keberadaan logam kompetitor ini diasumsikan telah menghambat proses fenol untuk tertranspor ke fasa penerima. Kata kunci: Kopoli(eugenol-DVB), Polymer Inclusion Membrane (PIM), transpor fenol Phenol is a toxic organic compound, dangerous and hardly degradable which is commonly found as the waters pollutants. The study of phenol transport using the Polymer Inclusion Membrane (PIM) method with copoly(eugenol-DVB) as the carrier compound was carried out to resolve this problems. Some parameters that influence phenol transport have been investigated, including the pH of the source phase phenol, receiver phase NaOH concentration, PIM membrane thickness and transport time. Synthesis of copoly(eugenol-DVB) was carried out using a copolymerization reaction between eugenol with 10% divinylbenzene (DVB), and BF3O(C2H5)2 as the catalyst. The copolymer powder produced was characterized using FT-IR. The concentration of phenol after transport was determined by UV�Vis spectrophotometry using 4-amino antipyrine reagents and the absorbance was measured at wavelength λ = 456 nm. The results showed that PIM membranes with copoly(eugenol-DVB) as carrier compounds were able to transport phenol effectively by 89.40% at optimum conditions: pH of the source phase phenol 5.5, 0.1 M NaOH concentration, T27 type PIM membrane thickness and transport time for 24 hours. PIM membranes that have been used for transport for 24 hours were characterized using SEM and FT-IR. Phenol transport with metal competitor Cu (II) and Pb (II) resulted in a smaller concentration of transported phenol compared to metalless transport of 27.25%. The existence of metal as the competitor is assumed to have inhibited the phenol process to be transported to the receiving phase. Keywords : Copoly(eugenol-DVB), Phenol transport, Polymer Inclusion Membrane (PIM)

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika > 540 Kimia dan ilmu yang berhubungan
Program Studi:	FAKULTAS MIPA > Prodi Kimia
Pengguna Deposit:	UPT . Digilib2
Date Deposited:	29 Mar 2022 13:11
Terakhir diubah:	29 Mar 2022 13:11
URI:	http://digilib.unila.ac.id/id/eprint/56692

Actions (login required)

Lihat Karya Akhir