PERANCANGAN DAN PEMBUATAN ALAT JOMINY TEST STANDAR ASTM A 255-2 DENGAN MATERIAL UJI BAJA KARBON SEDANG AISI 1045

AKHMAD YASSER YASRIZAL, 1215021011 (2019) PERANCANGAN DAN PEMBUATAN ALAT JOMINY TEST STANDAR ASTM A 255-2 DENGAN MATERIAL UJI BAJA KARBON SEDANG AISI 1045. FAKULTAS TEKNIK, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK.pdf Download (180Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya staf Download (4Mb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (4Mb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Pembentukan struktur martensit pada baja karbon dapat meningkatkan sifat mekanik suatu bahan salah satunya yaitu kekerasanya, dimana material baja karbon tersebut dilakukan perlakuan panas dengan dipanaskan pada temperatur austenit dan didinginkan dengan cepat. Laju pendinginan dan kadar karbon akan mempengaruhi struktur mikro yang terbentuk seperti martensit, ferit dan perlit. Tujuan penelitian ini adalah membuat alat Jominy Test. Data yang didapat dari pengujian kekerasan dianalisis untuk mendapatkan harga peningkatan kekerasan dari material baja karbon sedang. Kemudian data hasil yang diperoleh dimasukan ke dalam hardenability band (pita mampukeras) yang sudah standar, apakah masuk kedalam range yang ada atau tidak. Peningkatan kekerasan pada baja karbon sedang sebesar 50%. Dari data yang didapat, menunjukan bahwa kadar karbon sangat berpengaruh dalam peningkatan kekerasan suatu baja. Secara umum hasil penelitian menunjukan rancangan alat Jominy Test sudah layak digunakan, dengan asumsi tinggi semprotan air pada nozel setinggi 6.5 cm dan jarak antara spesimen dengan nozel 12.7 mm. Kata kuci : Martensit, Hardenability band, austenit, Jominy Test The formation of a martensitic structure on carbon steel can improve the mechanical properties of a material, one of which is its hardness, where the carbon steel material is heat treated by being heated at austenite temperature and cooled quickly.The cooling rate and carbon content will affect the micro structures formed such as martensite, ferrite and pearlite.The purpose of this study was to make a Jominy Test. Data obtained from hardness tests were analyzed to get the price of increased hardness of medium carbon steel material.Then the results data obtained is entered into the standard hardenability band.whether it is in the range or not. Increased hardness in medium carbon steel by 50%. From the data obtained, it shows that carbon content is very influential in increasing the hardness of a steel. In general, the results of the study show that the design of the Jominy Test tool is feasible to use, assuming the water spray height on the nozzles is as high as 6.5 cm and the distance between the specimens and the nozzles is 12.7 mm. Keywords: Martensit, Hardenability band, austenit, Jominy Test

Jenis Karya Akhir:	Skripsi
Subyek:	600 Teknologi (ilmu terapan) > 620 Ilmu teknik dan ilmu yang berkaitan
Program Studi:	Fakultas Teknik > Prodi S1-Teknik Mesin
Pengguna Deposit:	UPT . Digilib2
Date Deposited:	31 Mar 2022 03:58
Terakhir diubah:	31 Mar 2022 03:58
URI:	http://digilib.unila.ac.id/id/eprint/56968

Actions (login required)

Lihat Karya Akhir