ANGGA AMIRAJ NURPRATAMA, 1315021007 (2019) SIFAT TARIK KOMPOSIT SERAT ACAK HYBRID BAGASSE/KACA/POLYESTER. FAKULTAS TEKNIK, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK.pdf Download (1186Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya staf Download (1503Kb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (1504Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Perkembangan teknologi komposit semakin berkembang pesat. Namun pada umumnya hal tersebut di dominasi pengembangan komposit sintetik dibandingkan komposit natural. Hal ini dikarenakan komposit natural memiliki sifat mekanik cenderung lebih rendah, oleh karena itu perlu adanya upaya peningkatan kualitas pada komposit natural. Maka dari itu penelitian ini bertujuan untuk meningkatkan kekuatan mekanik komposit natural dengan menggabungkan serat baggase dan kaca (Hybrid) pada satu campuran komposit untuk menghasilkan sifat mekanik yang lebih baik dibandingkan komposit non hybrid. Penelitian ini dilakukan di Laboratorium Komposit, Universitas Lampung. Pembuatan komposit menggunakan metode hands lay up dengan matrik poliester. Variasi pertama dengan komposisi 70% matrik poliester, 15% partikel baggase 15% serat kaca, variasi yang kedua dengan 80% matrik poliester, 10% paritkel baggase, 10% serat kaca dan variasi terakhir terdiri dari 90% matrik poliester ,5% partikel baggase, 5% serat kaca.dilakukan pengujian tarik berstandar ASTM D�638. Hasil dari penelitian terbaik terdapat pada variasi 70:15:15 dengan nilai σu = 74.266 MPa, ε = 0.016 dan E = 3.601 GPa. kenaikan fraksi volume serat kaca dan partikel baggase meningkatkan nilai modulus elastis dan kekuatan tarik. Kemudian bedasarkan pengamatan menggunakan metode Scanning Electron Microscope ikatan yang dimiliki serat baggase terhadap matrik lebih baik dibandingkan dengan serat kaca. Kata Kunci : Komposit Hybrid, E-Glass, Baggase, Sifat Mekanik, ASTM-D638, Scanning Electron Microscope The development of composite technology was increasingly advanced. But in general this is dominated by the development of synthetic composites compared to natural composites. This is because natural comoposite have lower mechanical properties, therefore there is a need to improve the quality of natural composites. Therefore, this study aims to improve the mechanical strength of natural composites by combining baggase and glass fibers in one composite mixture to produce better mechanical properties than non hybrid composites. This research was conducted in Composite Laboratory University of Lampung. Hands lay up method was used to fabricated the composite. The first variation with a composition of 70% polyester,15% baggase particle, 15% glass fiber, the second variation with 80% polyester matrix,10% baggase particle, 10% glass fiber and the final variation consists of 90% polyester matrix, 5% baggase particle, 5% glass fiber. The tensile test was carried out according to ASTM-D638 standard. The best result can be found in variations of 70:15:15 with a value of σu = 74.266 MPa, ε = 0.016 and E = 3.601 GPa. The modulus elastic and tensile strength of hybrid composite were increase with fiberglass and bagasse particle volume fraction. Based on observations using the scanning electron microscope method, the bonding of baggase fiber to matrix is better than glass fiber. Keywords:Hybrid composite, Fiberglass, Baggase fiber, Mechanical properties, ASTM-D638, Scanning Electron Microscope

Jenis Karya Akhir:	Skripsi
Subyek:	600 Teknologi (ilmu terapan) > 620 Ilmu teknik dan ilmu yang berkaitan
Program Studi:	Fakultas Teknik > Prodi S1-Teknik Mesin
Pengguna Deposit:	UPT . Digilib2
Date Deposited:	31 Mar 2022 03:58
Terakhir diubah:	31 Mar 2022 03:58
URI:	http://digilib.unila.ac.id/id/eprint/57014

Actions (login required)

Lihat Karya Akhir