OPTIMISASI PENGARUH KOMPOSISI SILIKA, KAOLIN, KALSIUM OKSIDA, DAN SERAT KARBON TERHADAP SIFAT MEKANIK KOMPOSIT GEOPOLIMER

MUHAMAD KRESNA ISMOYO. SNF, 1315021042 (2019) OPTIMISASI PENGARUH KOMPOSISI SILIKA, KAOLIN, KALSIUM OKSIDA, DAN SERAT KARBON TERHADAP SIFAT MEKANIK KOMPOSIT GEOPOLIMER. FAKULTAS TEKNIK, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK.pdf Download (14Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya staf Download (3939Kb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (3244Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Geoplimer adalah meterial yang disintesis dari bahan dasar dengan kandungan unsur silika dan alumina dalam jumlah besar. Dalam pengaplikasiannya, geopolimer banyak digunakan sebagai pengganti semen portland. Selain itu, Geopolimer juga dapat digunakan sebagai material dalam pembuatan pipa. Tetapi secara keseluruhan geopolimer memiliki ketangguhan dan sifat mekanik yang rendah jika dibandingkan dengan dengan logam ataupun keramik. Penelitian ini dilakukan sebagai upaya untuk menghasilkan material komposit geopolimer dengan sifat mekanik yang baik dan dapat diaplikasikan sebagai material dalam pembuatan pipa ramah lingkungan, dengan cara mengoptimisasi komposisi bahan dasar gopolimer. Dihasilkan komposisi yang menghasilkan nilai Flexural Strength rata-rata terbaik sebesar 41,46 MPa adalah pada komposisi T9 yaitu dengan rincian Silika 27 gr, Kaolin 55 gr, CaO 6 gr, dan Serat Karbon 13 gr. Dan Hoop Tensile yang dilakukan pada komposisi T8 yaitu dengan rincian Silika 27 gr, Kaolin 55 gr, CaO 6 gr, dan Serat Karbon 13 gr. Dihasilkan nilai Hoop Tensile Strength terbaik sebesar 5,49MPa. Berdasarkan analisis taguchi komposisi geopolimer optimum yang dihasilkan adalah pada Silika 25 gr, Kaolin 55 gr, CaO 6 gr, dan Serat Karbon 13 gr. dan diprediksi menghasilkan nilai S/N ratio sebesar 33,55 Kata kunci : Geopolimer, Flexural Strength, Hoop Tensile Strength, Metode Taguchi Geoplimer is a meterial which is synthesized from basic materials with large amounts of silica and alumina. In its application, geopolymers are widely used as a substitute for portland cement. In addition, Geopolymers can also be used as material in making pipes. But overall geopolymers have low toughness and mechanical properties when compared to metals or ceramics. This research was conducted as an effort to produce geopolymer composite materials with good mechanical properties and can be applied as material in making environmentally friendly pipes, by optimizing the composition of the basic ingredients of gopolymers. The resulting composition that produces the best Flexural Strength value of 41.46 MPa is in the T9 composition, namely with the details of Silica 27 gr, Kaolin 55 gr, CaO 6 gr, and Carbon Fiber 13 gr. And Hoop Tensile carried out on the composition of T8, namely with details of Silica 27 gr, Kaolin 55 gr, CaO 6 gr, and Carbon Fiber 13 gr. The best Hoop Tensile Strength value is 5.49MPa. Based on the taguchi analysis the optimum geopolymer composition produced was 25 grams of Silica, 55 grams of Kaolin, 6 grams of CaO, and 13 grams of Carbon Fiber. and predicted to produce an S / N ratio of 33.55. Key Words : Geopolymer, Flexural Strength, Hoop Tensile Strength, Taguchi Methods.

Jenis Karya Akhir:	Skripsi
Subyek:	600 Teknologi (ilmu terapan) > 620 Ilmu teknik dan ilmu yang berkaitan
Program Studi:	Fakultas Teknik > Prodi S1-Teknik Mesin
Pengguna Deposit:	UPT . Teti Novianti
Date Deposited:	31 Mar 2022 10:28
Terakhir diubah:	31 Mar 2022 10:28
URI:	http://digilib.unila.ac.id/id/eprint/57029

Actions (login required)

Lihat Karya Akhir