PENGARUH KOMPOSISI KARBON AKTIF PADA PROSES CARBURIZING TERHADAP KEKERASAN DAN KOMPOSISI KIMIA PADA BAJA ST41

RIZKI AKBARI, 1215021067 (2019) PENGARUH KOMPOSISI KARBON AKTIF PADA PROSES CARBURIZING TERHADAP KEKERASAN DAN KOMPOSISI KIMIA PADA BAJA ST41. FAKULTAS TEKNIK, UNIVERSITAS LAMPUNG.

Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf.pdf Download (14Mb) | Preview
	File PDF SKRIPSI FULL.pdf.pdf Restricted to Hanya staf Download (20Mb)
Preview	File PDF ABSTRAK.pdf Download (8Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Carburizing adalah suatu proses perlakuan panas dimana material menyerap karbon dari arang maupun karbon monoksida. Secara umum pack carburizing merupakan proses pengerasan permukaan dengan penambahan unsur karbon pada permukaan material. Metode ini juga menguntungkan dan banyak digunakan untuk proses pengerasan permukaan pada baja karbon rendah. Pada pengujian ini menggunakan baja karbon rendah ST41 dengan komposisi karbon aktif (60%, 70%, 80%, 90%) dan variasi katalisator(40%, 30%, 20%, 10%) untuk mencari kekerasan dan komposisi kimia. Temperature pemasan pada proses carburizing 850oC dengan waktu penahanan 30 menit dan proses pendinginan cepat (quenching). Penambahan nilai kekerasan pada saat di carburizing yaitu kekerasaan terbaik pada komposisi arang 60% dan katalis 40%. Dan bertambah komposisi kimia di Variasi yang sama Kata kunci: pack carburizing, Komposisi kimia, ST41, difusi Carburizing was a heat-treatment process in which materials absorb carbon from both charcoal and carbon monoxide.Generally pack carburizing is a surface hardening process with the addition of carbon particles to the material surface. The method is also profitable and is widely used for the surface hardening process of low-carbon steel. This test USES st41 low-carbon steel with active carbon composition (60%, 70%, 80%, 90%) and catalytic variations (40%, 30%, 20%, 10%) in search of violence and chemical composition. Temperature enlarging the carburizing 850oc with 30 minute detention time and rapid cooling process (quenching). The increased violence value at carburizing was the best compression of arang 60% and the 40% catalyst. And increasing the chemical composition in the same variation. Key word: pack carburizing, chemical composition, ST41, difusi

Jenis Karya Akhir:	Skripsi
Subyek:	600 Teknologi (ilmu terapan) > 620 Ilmu teknik dan ilmu yang berkaitan
Program Studi:	Fakultas Teknik > Prodi S1-Teknik Mesin
Pengguna Deposit:	UPT . Teti Novianti
Date Deposited:	31 Mar 2022 18:53
Terakhir diubah:	31 Mar 2022 18:53
URI:	http://digilib.unila.ac.id/id/eprint/57082

Actions (login required)

Lihat Karya Akhir