PENGARUH PENAMBAHAN SERAT LENGKUAS TERHADAP KEKUATAN TARIK KOMPOSIT SERAT LENGKUAS/EPOKSI

ANGGI ANTONIUS, 1315021008 (2019) PENGARUH PENAMBAHAN SERAT LENGKUAS TERHADAP KEKUATAN TARIK KOMPOSIT SERAT LENGKUAS/EPOKSI. FAKULTAS TEKNIK, UNIVERSITAS LAMPUNG.

[img]
Preview
FIle PDF
ABSTRAK.pdf

Download (11Kb) | Preview
[img] FIle PDF
SKRIPSI FULL.pdf
Restricted to Hanya staf

Download (2695Kb)
[img]
Preview
FIle PDF
SKRIPSI TANPA BAB PEMBAHASAN.pdf

Download (1024Kb) | Preview

Abstrak

Serat lengkuas (alpinia galangal) dapat dimanfaatkan menjadi penguat komposit serat alami karena memiliki kekuatan tarik yang tinggi. Penelitian ini bertujuan untuk mengetahui pengaruh serat lengkuas terhadap kekuatan tarik komposit serat lengkuas. Komposit ini dapat diaplikasikan di berbagai bidang seperti otomotif, alat rumah tangga dan lain sebagainya. Komposit dibuat dari pencampuran serat lengkuas dengan matrik polimer epoksi. Serat lengkuas diberikan perlakuan alkali 5% NaOH selama dua jam dan dibersihkan dengan aquades lalu dikeringkan. Serat disusun secara acak (random) dengan fraksi massa serat 2%, 3%, dan 4%, dengan panjang serat yaitu 30 mm. Pencetakan spesimen dengan metode vacuum resin infusion. Untuk mengetahui sifat mekanik dari komposit serat lengkuas dilakukan pengujian kekuatan tarik sesuai standar pengujian ASTM D 638-03 dan untuk mengetahui morfologi patahan komposit dilakukan dengan pengamatan mikroskop dan scanning electron microscope. Dari hasil pengujian material komposit serat lengkuas, didapat kekuatan tarik tertinggi pada sampel fraksi massa 4% dengan nilai 26,89 MPa, nilai regangan sebesar 5,03% dan modulus elastisitas sebesar 0,68 GPa. Pada hasil pengamatan mikroskop dan scanning electron microscope, terdapat fiber breaking dipermukaan patahan dimana polimer dan serat putus secara bersamaan yang artinya bounding serat dengan polimernya baik. Beberapa spesimen terdapat pull out dan void yang terjebak di beberapa spesimen, hal inilah yang menyebabkan kekuatan tarik komposit tidak lebih kuat dari spesimen epoksi murni, Namun Penggunaan serat lengkuas dapat mempengaruhi kekuatan tarik komposit dimana terjadi peningkatan di setiap penambahan massa serat. Kata Kunci : alpinia galangal, komposit, polimer, kekuatan tarik, regangan, modulus elastisitas. Alpinia Galangal fiber can be used as an reinforcement for natural fiber composite because it has high tensile strength. This research aim to know the effect of Alpinia Galangal fiber on the tensile strength of the Alpinia Galangal Fiber composite. This composite can be applied in multiple field as automotive, household, and etc. Composite are made by mixing Alpinia Galangal fiber with epoxy polimer matrix. Alpinia Galangal fiber was given an alkali treatment for two hours and cleaned using distilled water and then was dried. The fibers were arranged randomly according to 2%, 3%, and 4% fiber mass fraction. The length of fibers is 30 mm. The specimen printing method was vacuum resin infusion. Mechanical properties Alpinia Galangal fiber composites, tensile strength was tested according to ASTM D 638-03 standard test method. The composite morphology of the breaking composite was observed using optical microscope Scanning Electron Microscope. Tensile strength of Alpinia Galangal fiber composite,Shows the highest tensile strength at mass fraction of 4%, it was 26,89 MPa, the strain was 5,03% and elastic modulus was 0,68 GPa. The observation with optical microscope and scanning electron microscope found the fiber breaking on the fracture surface. At fiber breaking, fiber and polymer broke at the same time. Many specimen were found pull out and the present of void. It causes tensile strength of fiber composite was less than pure epoxy. The use of Alpinia Galangal fiber can affect composite tensile strength. Keywords: Alpinia Galangal, composite, polymer, ASTM D 638-03, tensile strength, young modulus.

Jenis Karya Akhir: Skripsi
Subyek: 600 Teknologi (ilmu terapan) > 620 Ilmu teknik dan ilmu yang berkaitan
Program Studi: Fakultas Teknik > Prodi S1-Teknik Mesin
Pengguna Deposit: UPT . Digilib2
Date Deposited: 31 Mar 2022 04:13
Terakhir diubah: 31 Mar 2022 04:13
URI: http://digilib.unila.ac.id/id/eprint/57110

Actions (login required)

Lihat Karya Akhir Lihat Karya Akhir