PENGGUNAAN KOMPOSIT GEOPOLIMER UNTUK PIPA TAHAN PANAS DAN KOROSI

ARIZON, 1315021010 (2019) PENGGUNAAN KOMPOSIT GEOPOLIMER UNTUK PIPA TAHAN PANAS DAN KOROSI. FAKULTAS TEKNIK, UNIVERSITAS LAMPUNG.

[img]
Preview
FIle PDF
ABSTRAK.pdf

Download (7Kb) | Preview
[img] FIle PDF
SKRIPSI FULL.pdf
Restricted to Hanya staf

Download (2885Kb)
[img]
Preview
FIle PDF
SKRIPSI TANPA BAB PEMBAHASAN.pdf

Download (2144Kb) | Preview

Abstrak

Perpipaan merupakan sarana transportasi untuk mengalirkan fluida. Dalam kondisi tertentu dibutuhkan pipa yang tahan terhadap korosi, endapan kerak dan temperatur panas. Masalah yang muncul pada penggunaan pipa baja ialah laju korosi dan endapan kerak yang tinggi, sedangkan penggunaan pipa PVC (Berbahan Plastik) tidak tahan terhadap temperatur panas. Penelitian ini merupakan suatu upaya untuk mandapatkan material yang tahan terhadap panas dan korosi. Material yang digunakan adalah silika sekam padi, yang kemudian dicampurkan dengan bahan-bahan komposit geopolimer lainnya. Dengan metode taguchi dilakukan eksperimen dalam jumlah yang banyak untuk mendapatkan sampel terbaik. Dihasilkan komposisi terbaik yang menghasilkan Flexural Strength rata-rata 58,16 Mpa, dengan komposisi 27 gr Silikon Dioksida, 51 gr Kaolin, 9 gr CaO, 13 gr serat karbon, 22,5 gr Sodiuim Silikat dan 7,5 gr Sodium Hidroksida. Kemudian komposisi optimum tersebut digunakan untuk pencetakan pipa geopolimer dengan cara Centrifugal Casting. Didapatkan hasil pengujian Hoop Tensile Strength dengan rata-rata 0,76 MPa. Berdasarkan analisis Taguchi komposisi komposit geopolimer optimum yang dihasilkan adalah 33 gr Silikon Dioksida, 51 gr Kaolin, 9 gr CaO, 13 gr Serat Karbon, 22,5 gr Sodium Silikat dan 7,5 gr Sodium Hidroksida. Kata Kunci : Geopolimer, Pipa, Flexural Strength, Hoop Tensile Strength, Metode Taguchi, Centrifugal Casting. Piping is a transportation means in draining fluid. In a certain condition, it is needed a pipe that is resistant to corrosion, scale deposits and heat themperature. The problems that appears by using steel pipe are the speed in corrosing and deposits in scaling. However, the use of PVC pipe (plastic pipe) is not resistant in heat themperature. This research is an attempt to obtain materials that is resistant to heat and corrosion. The materials used is rice husk silica, which is then mixed with other geopolymer composites materials. With the taguchi method a large number of experiments are performed to get the best sample. It gets the best composition which gets Flexural Strength with average 58,16 Mpa, the composistion are 27 gr of Silicon Dioxide, 51 gr Caolin, 9 gr CaO, 13 gr Carbon Fiber, 22,5 gr Sodium Silicate and 7,5 gr Sodium Hidroksida. After that, the optimum composition is used in printing the geopolymer pipe by Centrifugal Casting method. It gets the test result Hoop Tensile Strength with average 0,76 Mpa. According to the Taguchi analysis, the optimum composition of the geopolymer composites that is generated are 33 gr Silicon Dioxide, 51 gr Caolin, 9 gr CaO, 13 gr Carbon Fiber, 22,5 gr Sodium Silicate and 7,5 gr Sodium Hidroksida. Keyword : Geopolymer, Pipe, Flexural Strength, Hoop Tensile Strength, Taguchi Method, Centrifugal Casting.

Jenis Karya Akhir: Skripsi
Subyek: 600 Teknologi (ilmu terapan) > 620 Ilmu teknik dan ilmu yang berkaitan
Program Studi: Fakultas Teknik > Prodi S1-Teknik Mesin
Pengguna Deposit: UPT . Digilib2
Date Deposited: 31 Mar 2022 04:13
Terakhir diubah: 31 Mar 2022 04:13
URI: http://digilib.unila.ac.id/id/eprint/57124

Actions (login required)

Lihat Karya Akhir Lihat Karya Akhir