SINTESIS DAN KARAKTERISASI SENYAWA BASA SCHIFF DARI SALISILALDEHIDA DAN ETILENDIAMINA SEBAGAI SENSITIZER DENGAN VARIASI ELEKTROLIT GEL DALAM KINERJA DYE SENSITIZED SOLAR CELLS (DSSC)

TRI JULIANTI, 1517011067 (2019) SINTESIS DAN KARAKTERISASI SENYAWA BASA SCHIFF DARI SALISILALDEHIDA DAN ETILENDIAMINA SEBAGAI SENSITIZER DENGAN VARIASI ELEKTROLIT GEL DALAM KINERJA DYE SENSITIZED SOLAR CELLS (DSSC). Fakultas Matematika dan Ilmu Pengetahuan Alam, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK.pdf Download (1773Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya staf Download (1772Kb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (1773Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Telah dilakukan penelitian tentang sintesis senyawa basa Schiff dari salisilaldehida dan etilendiamina sebagai sensitizer dengan variasi elektrolit gel pada Dye Sensitized Solar Cell (DSSC) menggunakan metode kondensasi. Karakterisasi menggunakan spektrofotometri UV-Vis, FT-IR dan analisis dekomposisi termal menggunakan DTA/TGA lalu diaplikasikan pada DSSC dengan variasi konsentrasi larutan elektrolit gel PEG 0,025 M, 0,05 M dan 0,1 M.. Penelitian ini bertujuan untuk mengetahui nilai kuat arus, tegangan dan efisiensi dari senyawa basa Schiff sebagai sensitizer. Hasil sintesis senyawa basa Schiff diperoleh padatan kristal berwarna kuning cerah dengan rendemen 81,14 %. Karakterisasi menggunakan UV-Vis menunjukan adanya pergeseran panjang gelombang maksimum (λmaks) yang memiliki transisi n → π* dari gugus azometina senyawa basa Schiff sebesar 335 nm. Hasil data spektrum IR senyawa basa Schiff menunjukkan adanya vibrasi ikatan gugus azometina (>C=N-) pada 1610,21 cm-1 . Hasil analisis DTA/TGA diperoleh pengurangan bobot massa yang berasal dari degradasi kerangka senyawa basa Schiff sebesar 97,2% pada rentang suhu 180 oC – 300 oC. Berdasarkan hasil analisis menggunakan spektrofotometri UV-Vis, spektrofotometri IR, dan DTA/TGA senyawa basa Schiff dapat digunakan sebagai sensitizer pada DSSC. Senyawa basa Schiff yang Hasil uji DSSC berdasarkan variasi konsentrasi larutan elektrolit gel PEG diperoleh kuat arus (mA) dan tegangan (mV) pada konsentrasi larutan PEG 0,1 M memiliki nilai efisiensi tertinggi sebesar 0,08% dengan kuat arus 0,8 mA dan tegangan 98,34 mV. Hasil pengukuran pada rangkaian DSSC menunjukkan bahwa senyawa basa Schiff dapat diaplikasikan pada DSSC. Kata Kunci : Basa Schiff, sensitizer, DSSC, DTA/TGA, elektrolit gel. Research about synthesize Schiff base compound from salicylaldehide and etylenediamine with variation of electrolyte gel on Dye Sensitized Solar Cell (DSSC) has been carried out using condensation method. Characterization utilized by UV-Vis spectrophotometry, FT-IR and thermal decomposition analysis using DTA/TGA and then applied to DSSC with variation concentration of gel electrolyte solution PEG 0.025 M, 0.05M, and 0.1 M. Aims of this research is to find out strong current, voltage, and efficiency value from Schiff base compound as sensitizer. Schiff base synthesis results obtained bright yellow crystalline solid with percent value of 81.14 %. Characterization using UV-Vis spectrophotometry indicated maximum wavelength shift of 335 nm that have a electronic transition n→π* from azometine group on Schiff base compound. IR spectra of Schiff base showed the presence of bond vibration due to azometine group in 1610.21 cm-1 . DTA/TGA analysis evidences reduction in mass weight that originated from framework degradation Schiff base compound of 97.2 % on temperature range of 180-300 C. Based on analysis result exert spectrophotometry of UV-Vis, IR and DTA/TGA showed that Schiff base can be used as sensitizer on DSSC. The results of DSSC test with variation concentration of gel electrolyte solution PEG were the yield have strong current (mA) and voltage (mV), PEG solution concentration of 0.1 M give highest efficiency value equal to 0.08%, strong current was 0.8 mA and the voltage in 98.34 mV. The measurement result in DSSC suite conclude that Schiff base compound can be applied on DSSC. Keywords : Schiff Base, sensitizer, DSSC, DTA/TGA, gel electrolyte

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika > 540 Kimia dan ilmu yang berhubungan
Program Studi:	FAKULTAS MIPA > Prodi Kimia
Pengguna Deposit:	UPT . Digilib2
Date Deposited:	31 Mar 2022 04:13
Terakhir diubah:	31 Mar 2022 04:13
URI:	http://digilib.unila.ac.id/id/eprint/57170

Actions (login required)

Lihat Karya Akhir