ANALISIS SIFAT LISTRIK BAHAN POLIANION Li2CoSiO4 YANG DISINTESIS DARI SILIKA SEKAM PADI DAN PRODUK DAUR ULANG KATODE BATERAI ION LITIUM

NI’MATIL MABARROH, 1417041061 (2019) ANALISIS SIFAT LISTRIK BAHAN POLIANION Li2CoSiO4 YANG DISINTESIS DARI SILIKA SEKAM PADI DAN PRODUK DAUR ULANG KATODE BATERAI ION LITIUM. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK.pdf Download (2499Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya staf Download (2593Kb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (2593Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Studi ini bertujuan untuk mengetahui pengaruh perlakuan termal terhadap sifat listrik bahan Li2CoSiO4 berbasis silika sekam padi dan produk daur ulang katode BIL yang meliputi energi band gap, konduktivitas, konstanta dielektrik, dan faktor rugi dielektrik. Daur ulang katode BIL dilakukan menggunakan metode hidrometalurgi, prosesnya meliputi dekomposisi lempeng katode BIL dan acid leaching untuk menghasilkan produk Li2CO3 dan Co(OH)2. Ekstraksi silika sekam padi dilakukan dengan metode ekstraksi alkalis. Li2CoSiO4 dipreparasi dengan menggunakan metode solid-state dengan perbandingan 1:1 kemudian disintering pada suhu 600, 700, 800 dan 900 °C. Energi band gap dikarakterisasi menggunakan UV-Vis DRS. Sedangkan, konduktivitas, konstanta dielektrik dan faktor rugi dielektrik diukur menggunakan LCR Meter. Nilai energi band gap yang diperoleh pada suhu 600, 700, 800 dan 900 oC masing-masing sebesar 5,09; 5,04; 5,00 dan 4,97 eV. Nilai tersebut menunjukkan bahwa semakin tinggi suhu sintering, energi band gap pada sampel Li2CoSiO4 semakin kecil. Hal ini dimungkinkan adanya perubahan struktur kristal dari fasa βI ke γ0. Menurunya nilai energi band gap diikuti dengan peningkatan nilai konduktivitas listrik, penurunan konstanta dielektrik dan karakteristik yang berbeda ditunjukkan pada faktor rugi dielektrik. Pada frekuensi rendah, cenderung ada peningkatan dan pada frekuensi yang lebih tinggi, cenderung mengalami penurunan. Kata Kunci: limbah baterai, katode Li2CoSiO4, sifat listrik, silika sekam padi This study aims to determine the effect of thermal treatment on the electrical properties of Li2CoSiO4 based silica rice husks and Lithium-Ion Battery (LIB) cathode recycling products which include band gap energy, conductivity, dielectric constant, and dielectric loss factor. LIB cathode recycling was carried out by the hydrometallurgical method, the process includes the decomposition of LIB cathode scraps and acid leaching to produce Li2CO3 and Co(OH)2 products. Extraction of silica rice husk was carried out by the alkalis extraction method. Li2CoSiO4 was prepared by the solid-state method with a ratio of 1:1 then sintered at temperatures of 600, 700, 800 and 900 °C. The band gap energy was characterized using DRS UV-Vis. Meanwhile, conductivity, dielectric constant and dielectric loss factor were measured using LCR Meter. The band gap energy values obtained at temperatures of 600, 700, 800 and 900 oC were 5.09; 5.04; 5.00 and 4.97 eV, respectively. This value shows that the higher the sintering temperature, the band gap energy in the Li2CoSiO4 sample is getting smaller. This indicates a change from the βI phase to γ0. Decreasing the band gap energy value is followed by an increase in the value of electrical conductivity, a decrease in the dielectric constant and different characteristics shown in the dielectric loss factor. At low frequencies, there tends to be an increase and at higher frequencies, it tends to decrease. Keywords: Battery waste, electrical properties, Li2CoSiO4 cathode, rice husk silica

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika 500 ilmu pengetahuan alam dan matematika > 530 Fisika
Program Studi:	FAKULTAS MIPA > Prodi Fisika
Pengguna Deposit:	UPT . Teti Novianti
Date Deposited:	01 Apr 2022 04:55
Terakhir diubah:	01 Apr 2022 04:55
URI:	http://digilib.unila.ac.id/id/eprint/57326

Actions (login required)

Lihat Karya Akhir