SIFAT FISIS KOMPOSIT POLIETILEN/NANOTITANIA SEBAGAI FUNGSI KETEBALAN

NOLA FRICILIA, 1417041063 (2019) SIFAT FISIS KOMPOSIT POLIETILEN/NANOTITANIA SEBAGAI FUNGSI KETEBALAN. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK.pdf Download (92Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya staf Download (1161Kb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (1161Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Telah dilakukan penelitian tentang sifat fisis komposit PE/nanotitania sebagai fungsi ketebalan. Bahan yang digunakan adalah PE dan nanotitania. Pencampuran polietilen dan nanotitania dilakukan dengan pelelehan polietilen pada suhu 95 °C selama 5 menit kemudian ditambahi nanotitania 5 wt% dan 10 wt% dan dipanaskan pada suhu 124 °C selama 30 menit. Selanjutnya dicetak menggunakan barcoater dengan ukuran 6, 12 dan 25 μm dengan empat kali pengulangan. Variasi dilakukan untuk mengetahui pengaruh ketebalan komposit polietilen/nanotitania terhadap sifat listrik dan gugus fungsi. Hasil FTIR menunjukkan seiring bertambah ketebalan sampel serapan semakin sedikit dan muncul gugus fungsi baru yaitu hidroksil dan karbonil. Hasil LCR menunjukkan nilai konduktivitas terkecil yaitu sampel PE/nanotitania 5 wt% dengan ukuran 6 μm dan terbesar sampel PE/nanotitania 10% dengan ukuran 25 μm masing- masing sebesar 2,302 x 10-5 S/m dan 3,121 x 10-5 S/m pada frekuensi 105 Hz. Sedangkan nilai konstanta dielektrik terbesar yaitu sampel PE/nanotitania 5 wt% dengan ukuran 6 μm dan terkecil sampel PE/nanotitania 10 wt% dengan ukuran 6 μm pada frekuensi 105 Hz. Berdasarkan karakteristik tersebut, sampel PE/nanotitania 5 wt% dengan ukuran 6 μm merupakan material dengan sifat dielektrik terbaik sehingga sampel tersebut berpotensial untuk dimanfaatkan sebagai isolator kabel. Kata kunci: Komposit, PE, TiO2, konduktivitas dan konstanta dielektrik. Physical properties of polyethylene (PE)/nanotitania composite as a function of thickness have been studied. The material used is PE and nanotitania. The blending of PE with nanotitania was carried out by melting polyethylene at 95 °C for 5 minutes then added nanotitania 5 wt% and 10 wt% and heated at 124 ° C for 30 minutes. Then printed using barcoater with size 6, 12 and 25 μm with four repetitions. Variations were performed to determine the effect of composite thickness of polyethylene/ nanotitania on electrical properties and functional groups. FTIR results show that as the thickness of the absorption sample increases, new functional groups appear, namely hydroxyl and carbonyl. The LCR results show the smallest conductivity value, sample 5 wt% PE / nanotitania with 6 μm size and the largest 10% PE / nanotitania sample with a size of 25 μm each at 2,302 x 10-5 S/m and 3,121 x 10-5 S / m at a frequency of 105 Hz. While the largest dielectric constant value is a sample of PE/nanotitania 5 wt% with a size of 6 μm and the smallest sample PE/nanotitania 10 wt% with a size of 6 μm at a frequency of 105 Hz. Based on these characteristics, the 5 wt% PE/nanotitania sample with a size of 6 μm is the material with the best dielectric properties so that the sample has the potential to be used as a cable insulator. Key words. composite, PE, TiO2, conductivity and dielectric constant.

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika 500 ilmu pengetahuan alam dan matematika > 530 Fisika
Program Studi:	FAKULTAS MIPA > Prodi Fisika
Pengguna Deposit:	UPT . Teti Novianti
Date Deposited:	01 Apr 2022 04:55
Terakhir diubah:	01 Apr 2022 04:55
URI:	http://digilib.unila.ac.id/id/eprint/57331

Actions (login required)

Lihat Karya Akhir