PENINGKATAN KADAR DAN PEROLEHAN NIKEL HASIL REDUKSI SELEKTIF BIJIH NIKEL LATERIT KADAR RENDAH DENGAN ADITIF NATRIUM SULFIDA DAN REDUKTOR ANTRASIT DALAM PRODUKSI FERONIKEL

Riska Nadia Tirmayani, 1417041071 (2019) PENINGKATAN KADAR DAN PEROLEHAN NIKEL HASIL REDUKSI SELEKTIF BIJIH NIKEL LATERIT KADAR RENDAH DENGAN ADITIF NATRIUM SULFIDA DAN REDUKTOR ANTRASIT DALAM PRODUKSI FERONIKEL. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

[img]
Preview
File PDF
ABSTRAK-ABSTRACT.pdf

Download (326Kb) | Preview
[img] File PDF
SKRIPSI FULL.pdf
Restricted to Hanya staf

Download (3501Kb)
[img]
Preview
File PDF
SKRIPSI TANPA BAB PEMBAHASAN.pdf

Download (2618Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Telah dilakukan penelitian reduksi selektif bijih nikel laterit kadar rendah dengan menggunakan aditif natrium sulfida 10% berat dan reduktor antrasit 5%, 10% dan 15% berat. Penelitian ini dilakukan untuk mengetahui pengaruh temperatur, dosis reduktor antrasit dan waktu tahan reduksi terhadap kadar dan recovery besi nikel dalam ferronikel. Proses reduksi selektif dilakukan pada temperatur 950 oC, 1050 oC dan 1150 oC dengan waktu tahan selama 60 menit, 90 menit dan 120 menit diikuti dengan proses pemisahan magnetik untuk menghasilkan konsentrat dan tailing. Karakterisasi XRD hasil reduksi selektif menunjukkan fasa yang dominan seperti iron nickel (FeNi), iron sulfide (FeS), fayalite (Fe2SiO4) dan wuestite (FeO). Karakterisasi XRF menunujukkan nilai optimum yaitu pada temperatur 1150 oC dengan reduktor 10% dan waktu tahan reduksi selama 60 menit dengan kadar dan recovery nikel masing-masing sebesar 3,026% dan 89,32%. Ukuran partikel ferronikel pada sampel tersebut terbentuk dengan rata-rata ukuran butir sebesar 29,23. Kata kunci: bijih nikel laterit, reduksi selektif, uji karakterisasi. Experiments have been carried out selective reduction of low grade laterite nickel ore by using the additive sodium sulfide 10% by weight and a reductant anthracite 5%, 10% and 15% by weight. This study was conducted to determine the effect of temperature, anthracite and a reductant dose reduction resistant to high levels of iron and nickel in ferronickel recovery. The process of selective reduction carried out at a temperature of 950C, 1050C and 1150C with a holding time of 60 minutes, 90 minutes and 120 minutes followed by magnetic separation process to produce a concentrate and tailings. Characterization of selective reduction XRD results show that the dominant phase such as iron nickel (FeNi), iron sulfide (FeS), fayalite (Fe2SiO4) and wuestite (FeO). Characterization XRF shows optimum value at a temperature of 1150C with reductant 10% and holding time reduction for 60 minutes with a nickel grade and recovery respectively 3.026% and 89.32%. The particle size of ferronickel in the sample formed with an average grain size of 29,23μm. Keywords: nickel laterite ore, selective reduction, characterization test.

Jenis Karya Akhir: Skripsi
Subyek: 500 ilmu pengetahuan alam dan matematika
500 ilmu pengetahuan alam dan matematika > 530 Fisika
Program Studi: FAKULTAS MIPA > Prodi Fisika
Pengguna Deposit: UPT . Teti Novianti
Date Deposited: 01 Apr 2022 04:55
Terakhir diubah: 01 Apr 2022 04:55
URI: http://digilib.unila.ac.id/id/eprint/57342

Actions (login required)

Lihat Karya Akhir Lihat Karya Akhir