SINTESIS DAN KARAKTERSASI KALSIUM SILIKAT DENGAN MENGGUNAKAN METODE SOL-GEL

Salsabila Asy Syifa, 1417041076 (2019) SINTESIS DAN KARAKTERSASI KALSIUM SILIKAT DENGAN MENGGUNAKAN METODE SOL-GEL. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK.pdf Download (3959Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya staf Download (3959Kb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (3960Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Kalsium silikat telah berhasil disintesis dengan metode sol-gel menggunakan silika abu sekam padi dan kalsium nitrat, yang dikalsinasi pada suhu 800-1100 °C selama 3 jam. Hasil DTA menunjukkan adanya puncak eksotermik pada suhu 827 °C yang disebabkan oleh proses kristalisasi kalsium silikat, serta hasil TGA yang menunjukkan total penyusutan massa sebesar 23 %. Hasil XRD menunjukkan terbentuknya fase β-CaSiO3 dan α-CaSiO3 pada suhu 800 °C dengan intensitas yang semakin meningkat seiring bertambahnya suhu kalsinasi, dan mulai muncul fase CaSiO3 pada suhu 1100 °C sebagai fase minor. Hasil FTIR menunjukkan adanya puncak serapan dari gugus fungsi kalsium silikat yang ditandai dengan adanya ikatan Si-Ca-O. Morfologi SEM dari kalsium silikat memperlihatkan bentuk partikel seperti jarum (acicular), dengan ukuran partikel berkisar 0,44-0,68 μm, dan spektrum EDX yang menunjukkan unsur Ca, Si, dan O sebagai unsur penyusun senyawa kalsium silikat. Kata kunci: kalsium silikat, sol-gel, abu sekam padi, β-CaSiO3, α-CaSiO3, CaSiO3. Calcium silicate was successfully synthesized by the sol-gel method using silica rice husk ash and calcium nitrat, which was calcined at 800-1100 °C for 3 hours. The DTA results showed an exothermic peak at 827 °C caused by the crystallization process of calcium silicate, as well as the TGA results which showed a total weight loss of 23%. The XRD results show the formation of β- CaSiO3 and α-CaSiO3 phases at a temperature of 800 °C with increasing intensity as the calcination temperature increases, and the CaSiO3 phase starts at 1100 °C as a minor phase. FTIR results showed an absorption peak of the calcium silicate functional group characterized by the presence of Si-Ca-O bonds. SEM morphology of calcium silicate shows the shape of a particle like a needle (acicular), with particle sizes in the range of 0.44-0.68 μm, and EDX spectrum which shows elements of Ca, Si, and O as constituents of calcium silicate compounds. Keyword: Calsium silicate, sol-gel, rice husk ash, β-CaSiO3, α-CaSiO3, CaSiO3.

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika 500 ilmu pengetahuan alam dan matematika > 530 Fisika
Program Studi:	FAKULTAS MIPA > Prodi Fisika
Pengguna Deposit:	UPT . Teti Novianti
Date Deposited:	01 Apr 2022 04:55
Terakhir diubah:	01 Apr 2022 04:55
URI:	http://digilib.unila.ac.id/id/eprint/57346

Actions (login required)

Lihat Karya Akhir