PENGARUH LAJU PENGINJEKSIAN DOPING FLUOR TERHADAP AKTIVITAS FOTOKATALIS NANOTITANIA MENGGUNAKAN METODE SOL GEL

SRI RAHAYU, 1517041070 (2019) PENGARUH LAJU PENGINJEKSIAN DOPING FLUOR TERHADAP AKTIVITAS FOTOKATALIS NANOTITANIA MENGGUNAKAN METODE SOL GEL. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK.pdf Download (1234Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya staf Download (1334Kb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (1235Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Sintesis titania doping fluor (F-TiO2) dilakukan melalui metode sol-gel. Titanium isopropoksida (TTIP), tween-80, isopropanol dan ammonium fluorida (NH4F) sebagai sumber doping fluor digunakan sebagai bahan utama. Penelitian ini bertujuan untuk mempelajari pengaruh laju penginjeksian doping fluor menggunakan pompa injeksi terhadap aktivitas fotokatalis F-TiO2. Empat sampel doping fluor dipreparasi dengan laju penetesa masing-masing 0,4 ml/30 menit; 0,4 ml/60 menit; 0,4 ml/90 menit dan 0,4 ml/120 menit. Serbuk titania dikalsinasi pada suhu 450 oC selama 5 jam. Sampel yang disinter diuji untuk fotodegradasi remazol kuning di bawah sinar UV. Karakteristik fisika dianallisis menggunakan transmission electron microscopy (TEM) dan Spektrofotometer Uv-Vis. Hasil pengujian spektrofotometer UV-Vis menunjukkan bahwa ukuran partikel sampel dengan laju penginjeksian 0,4 ml/90 menit menunjukkan aktivitas fotokatalis yang lebih tinggi dengan ukuran partikel sebesar (14 ± 4) nm. Kata Kunci: Doping fluor, fotodegradasi, remazol kuning, titania. The F-doped titania was carried out through the sol-gel method. Titanium isopropoxide (TTIP), tween-80, isopropanol and ammonium fluoride (NH4F) as sources of doping fluorine were used as the main ingredients. This research aimed to study the effect of fluorine doping injection rate using injection pumps on F-TiO2 photocatalyst activity. Four fluorine doping samples were prepared with the respective penetration rate of 0.4 ml / 30 minutes; 0.4 ml / 60 minutes; 0.4 ml / 90 minutes and 0.4 ml / 120 minutes. The titania powder was calcined at 450 oC for 5 hours. The sintered sample was tested for photodegradation of remazol yellow under UV light. Physical characteristics were analyzed using transmission electron microscopy (TEM) and UV-Vis spectrophotometer. The results of the UV-Vis spectrophotometer showed that the particle size of samples with an injection rate of 0.4 ml / 90 minutes showed higher photocatalyst activity with particle sizes of (14 ± 4) nm. Keywords: Fluor doped, photodegradation,remazol yellow, titania.

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika > 530 Fisika
Program Studi:	FAKULTAS MIPA > Prodi Fisika
Pengguna Deposit:	UPT . Teti Novianti
Date Deposited:	01 Apr 2022 04:50
Terakhir diubah:	01 Apr 2022 04:50
URI:	http://digilib.unila.ac.id/id/eprint/57353

Actions (login required)

Lihat Karya Akhir