SIFAT FISIS KOMPOSIT PE/NANOSILIKA SEBAGAI FUNGSI KETEBALAN

TriaPermata Sari, 1417041092 (2019) SIFAT FISIS KOMPOSIT PE/NANOSILIKA SEBAGAI FUNGSI KETEBALAN. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK (ABSTRACT).pdf Download (450Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya staf Download (6Mb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (5Mb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Polietilena (PE) telah banyak digunakan sebagai bahan insulasi kabel tegangan tinggi karena sifat fisik, kimia, dan listriknya yang luar biasa. Dalam penelitian ini bubuk amorf nanosilika diekstraksi dari batu apung menggunakan NaOH, H2SO4 dan HCl. PE dan nanosilika dicampur menggunakan mixer pada suhu 95 oC dan kemudian dibuat lapisan tipis menggunakan barcoater. Presentase berat nanosilika adalah 5 dan 10% dengan ketebalan masing-masing 6, 12, dan 25 μm. PE/nanosilika dikarakterisasi melalui spektroskopi Fourier Transform Infra Red (FTIR) dan pengukuran LCR meter untuk mengetahui respon konduktivitas listrik dan permitivitas sebagai fungsi frekuensi. Efek ketebalan pada sifat listrik PE/nanosilika 5 dan 10% untuk nilai konduktivitas listrik pada sampel dengan ketebalan 25 μm memiliki nilai konduktivitas yang lebih besar. Sedangkan untuk permitivitas dari kedua sampel dengan variasi filer menunjukkan bahwa semakin tebal sampel, maka semakin besar nilai permitivitas. Kata Kunci: komposit, polietilena, nanosilika, barcoater. Polyethylene (PE) has been widely used as the insulation material of high voltage cables because of its outstanding physical, chemical, and electrical properties. In this research the amorph nanosilica powders were extracted from pumice using NaOH, H2SO4 and HCl. PE and nanosilica was blended by mixer at temperature 95 OC and then made the film by using barcoater. The weight percentage of nanosilica was 5 and 10% with thickness of 6, 12 and 25μm respectively. The PE/nanosilica were characterized via Fourier Transform Infra Red (FTIR) spectroscopy and LCR measurement to abtain conductivity and permitivity respons as a function of frequency. The effect thickness on the electrical properties of PE/nanosilica of 5 and 10 % for conductivity values in samples 25 μm thick has a greater conductivity value. Whereas for the electric constant of two filer variation shows that the thicker the sample, the greater the electric constant value. Whereas for the dielectric constant of two filler variations shows that the ticker the sample, the greater the electric constant value. Key words: composite, polyethylene, nanosilica, barcoater

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika 500 ilmu pengetahuan alam dan matematika > 530 Fisika
Program Studi:	FAKULTAS MIPA > Prodi Fisika
Pengguna Deposit:	UPT . Teti Novianti
Date Deposited:	01 Apr 2022 04:50
Terakhir diubah:	01 Apr 2022 04:50
URI:	http://digilib.unila.ac.id/id/eprint/57356

Actions (login required)

Lihat Karya Akhir