PENGARUH LAJU PENAMBAHAN DOPING FOSFOR TERHADAP STRUKTUR KRISTAL DAN LUAS PERMUKAAN SPESIFIK NANOTITANIA DENGAN METODE SOL GEL

Vidi Nurhidayah, 1517041095 (2019) PENGARUH LAJU PENAMBAHAN DOPING FOSFOR TERHADAP STRUKTUR KRISTAL DAN LUAS PERMUKAAN SPESIFIK NANOTITANIA DENGAN METODE SOL GEL. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK.pdf Download (1023Kb) | Preview
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (1023Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya staf Download (1022Kb)

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Telah dilakukan penelitian tentang pengaruh penambahan doping fosfor menggunakan syringe pump dengan metode sol-gel. Penelitian ini bertujuan untuk mengetahui pengaruh variasi laju penambahan doping fosfor terhadap struktur kristal dan luas permukaan spesifik TiO2. Laju penambahan doping yang digunakan selama 0,4; 0,2; 0,13 dan 0,1ml/jam dengan doping yang digunakan sebanyak 0,2 ml. Sampel TiO2 dikalsinasi pad suhu 450oC selama 5 jam. Serbuk dikarakterisasi dengan x-ray diffraction (XRD) dan surface area analyzer (SAA) dengan metode BET. Difraktogram XRD secara umum menunjukkan fasa struktur kristal nanotitania adalah anatase yang merupakan hasil sintesis TTIP sebagai sumber utama TiO2. Analisis ukuran partikel menggunakan data XRD pada TiO2 dengan laju yang berbeda-beda secara berturut-turut yaitu sebesar 10,13; 9,98; 9,25; dan 10,33 nm. Masing-masing hasil uji BET pada setiap sampel berturut- turut yaitu 86,9; 87,4; 99,7; 96,3dan 96,2 m 2 /g. Hasil ukuran partikel yaitu sebesar 9,25 nm dan luas permukaan maksimum pada metode BET yaitu sebesar 99,7 m 2 /g pada laju penetesan 0,2 ml/jam. Kata kunci: Luas permukaan, metode sol-gel, nanotitania, syringe pump. The effect of the addition of phosphorus dopingto nanotitania has been carried out using a syringe pump by sol-gel method. The purpose of this study is to determine the effect of the addition rate of phosphorus doping to thecrystal structure and specific surface area of TiO2. Doping increment rate used are 0,4; 0,2; 0,13 and 0,1 ml/hours. TiO2 samples were calcined at 450oC for 5 hours. The powder was characterized by x-ray diffraction (XRD) and surface area analyzer (SAA) by the BET method. XRD diffractogram shows that the nanotitania crystal structure phase is anatase which is the result of TTIP synthesis as the main source of TiO2. Particle size analysis using XRD data on TiO2 with different rates are 10.13; 9.98; 9.25; and 10.33 nm. Respectively BET test results for each sample were 86.9; 87,4; 99,7; 96,3and 96,2 m 2 /g. The average particle size is 9,25 nm and the maximum surface area in BET method was found 99,7 m2 /g in the rate of 0,2 ml/hours. Keywords: Nanotitania, sol-gel method, surface area, syringe pump.

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika 500 ilmu pengetahuan alam dan matematika > 530 Fisika
Program Studi:	FAKULTAS MIPA > Prodi Fisika
Pengguna Deposit:	UPT . Teti Novianti
Date Deposited:	01 Apr 2022 04:50
Terakhir diubah:	01 Apr 2022 04:50
URI:	http://digilib.unila.ac.id/id/eprint/57358

Actions (login required)

Lihat Karya Akhir