PENGARUH KOMPOSISI x TERHADAP STRUKTUR KRISTAL DAN SIFAT LISTRIK PADA BAHAN KATODE NaxFeSiO4 (x = 0,5; 1; 1,5; 2) BATERAI SODIUM BERBASIS SILIKA SEKAM PADI

AYU ASTIKA, 1517041027 (2019) PENGARUH KOMPOSISI x TERHADAP STRUKTUR KRISTAL DAN SIFAT LISTRIK PADA BAHAN KATODE NaxFeSiO4 (x = 0,5; 1; 1,5; 2) BATERAI SODIUM BERBASIS SILIKA SEKAM PADI. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

[img]
Preview
File PDF
ABSTRAK.pdf

Download (26Kb) | Preview
[img] File PDF
SKRIPSI FULL.pdf
Restricted to Hanya staf

Download (1264Kb)
[img]
Preview
File PDF
SKRIPSI TANPA BAB PEMBAHASAN.pdf

Download (988Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Studi ini bertujuan untuk menganalisis pengaruh komposisi x pada katode NaxFeSiO4 (x = 0,5; 1; 1,5; 2) berbasis silika sekam padi terhadap struktur kristal dan sifat listriknya. Sampel NaxFeSiO4 dibuat silika yang berasal sekam padi, Fe(NO3)3.9H2O, dan NaOH menggunakan metode sol-gel dengan komposisi Na sebanyak 0,5; 1; 1,5; 2 mol. Kemudian disinter pada suhu 700 °C dan ditahan selama 10 jam. Struktur kristal dikarakterisasi menggunakan X-Ray Diffraction (XRD), gugus fungsi dikarakterisasi menggunakan Fourier Transform Infrared (FTIR), energi band gap diuji menggunakan Ultraviolet Visible Diffuse Reflection (UV-Vis), dan konduktivitas listrik diuji menggunakan LCR-meter. Hasil karakterisasi FTIR menunjukkkan adanya puncak serapan yang berasal dari ikatan Si-O-Si, Fe-O, dan O-Na-O. Selanjutnya, hasil pengujian XRD mengindikasikan kehadiran fasa Fe2O3, Fe2SiO4 dan NaO2 pada sampel Na0,5FeSiO4 dan NaFeSiO4, sedangkan pada sampel Na1,5FeSiO4 dan Na2FeSiO4 menunjukkan kehadiran fasa Na2FeSiO4, SiO2, dan Na2SiO3. Pada sampel Na0,5FeSiO4 dan NaFeSiO4 didominasi oleh fasa Fe2O3, sedangkan pada sampel Na1,5FeSiO4 dan Na2FeSiO4 didominasi oleh fasa Na2FeSiO4. Seiring dengan bertambahnya komposisi Na, fasa Fe2O3 akan semakin menurun dan fasa Na2FeSiO4 akan semakin dominan keberadaannya di dalam sampel. Sementara itu, hasil pengujian UV-Vis DRS menunjukkan nilai energi band gap ganda pada sampel Na0,5FeSiO4 yaitu 2,03 eV dan 2,23 eV, pada sampel NaFeSiO4 yaitu 1,97 eV dan 2,19 eV serta pada sampel Na1,5FeSiO4 yaitu 2,15 eV dan 2,44 eV. Pada sampel Na2FeSiO4 dihasilkan energi band gap tunggal yaitu 2,11 eV. Perubahan nilai energi band gap tersebut diikuti dengan peningkatan nilai konduktivitas listrik pada sampel. Kata Kunci: Katode NaxFeSiO4, energi band gap, konduktivitas listrik, sekam padi, struktur kristal. This study aims to analyze the effect of x composition on the NaxFeSiO4 cathode (x = 0,5; 1; 1,5; 2) based on rice husk silica on its crystal structure and electrical properties. NaxFeSiO4 samples were made from rice husk silica, Fe(NO3)3.9H2O and NaOH using the sol-gel method with a composition of Na 0,5; 1; 1,5; 2 moles. Then, it was sintered at 700 °C and hold for 10 hours. The crystal structure was characterized by X-Ray Diffraction (XRD), the functional groups were characterized by Fourier Transform Infrared (FTIR), band gap energy was tested by Ultraviolet Visible Diffuse Reflection (UV-Vis), and electical conductivity was tested by LCR-meter. The result of FTIR characterization shows the absorption peaks originating from the Si-O-Si, Fe-O, and O-Na-O bonds. Furthermore, the XRD analysis indicating the presence of Fe2O3, Fe2SiO4, and NaO2 phases in Na0,5FeSiO4 and NaFeSiO4 samples, while in the Na1,5FeSiO4 and Na2FeSiO4 samples indicating presence of Na2FeSiO4, SiO2, and Na2SiO3 phases. Na0,5FeSiO4 and NaFeSiO4 samples are dominated by the Fe2O3 phase, whereas Na1,5FeSiO4 and Na2FeSiO4 samples are dominated by the Na2FeSiO4 phase. As Na composition increases, Fe2O3 phase will decrease and Na2FeSiO4 become more dominant in the samples. Meanwhile, the UV-Vis DRS analysis results shows the value of double energy band gap in the Na0,5FeSiO4 i.e 2,03 eV and 2,23 eV, NaFeSiO4 sample i.e 1,97 eV and 2,19 eV , as well as in the Na1,5FeSiO4 sample i.e. 2,15 eV and 2,44 eV. In the Na2FeSiO4 sample produced a single band gap energy i.e 2,11 eV. The change in the band gap energy value followed by an increase in the value of electrical conductivity in the samples. Keywords : NaxFeSiO4 cathode, band gap energy, electrical conductivity, rice husk, crystal structure.

Jenis Karya Akhir: Skripsi
Subyek: 500 ilmu pengetahuan alam dan matematika
500 ilmu pengetahuan alam dan matematika > 530 Fisika
Program Studi: FAKULTAS MIPA > Prodi Fisika
Pengguna Deposit: UPT . Teti Novianti
Date Deposited: 01 Apr 2022 04:51
Terakhir diubah: 01 Apr 2022 04:51
URI: http://digilib.unila.ac.id/id/eprint/57394

Actions (login required)

Lihat Karya Akhir Lihat Karya Akhir