PENGARUH PERLAKUAN TERMAL TERHADAP STRUKTUR KRISTAL DAN KARAKTERISTIK SIFAT LISTRIK PADA BAHAN POLIANION Na2FeSiO4 BERBASIS SILIKA SEKAM PADI

AYUNIS RIZQI AMALIA, 1517041101 (2019) PENGARUH PERLAKUAN TERMAL TERHADAP STRUKTUR KRISTAL DAN KARAKTERISTIK SIFAT LISTRIK PADA BAHAN POLIANION Na2FeSiO4 BERBASIS SILIKA SEKAM PADI. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK.pdf Download (3799Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya staf Download (3799Kb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (3800Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Sampel Na2FeSiO4 berhasil disintesis menggunakan metode sol-gel dari prekursor NaOH, Fe(NO3)3.9H2O, C6H8O7.H2O, dan silika sekam padi. Sampel disinter pada suhu 500-800 °C dengan waktu tahan selama 10 jam. Untuk mengidentifikasi struktur dan sifat listrik, sampel dikarakterisasi menggunakan FTIR, TG/DTA, XRD, DRS, dan LCR. Sejumlah gugus fungsi seperti Si-O, Na-O, Fe-O teridentifikasi dalam seluruh sampel. Analisis XRD menunjukkan bahwa fasa kristalin Na2FeSiO4 telah terbentuk pada suhu 500 °C. Selain itu, analisis XRD juga menunjukkan kemunculan fasa pengotor di dalam sampel, seperti Na2SiO3 dan SiO2. Peningkatan suhu sintering menyebabkan bertambahnya komposisi fasa Na2FeSiO4 di dalam sampel yang diikuti dengan meningkatnya nilai energi band gap dan menurunnya nilai konduktivitas listrik. Kata kunci: energi band gap, gugus fungsi, konduktivitas listrik, Na2FeSiO4, silika sekam padi, struktur kristal. Na2FeSiO4 samples were successfully synthesized using the sol-gel method from NaOH, Fe(NO3)3.9H2O, C6H8O7.H2O, and rice husk silica. The samples were sintered at a temperature of 500-800 °C with a holding time of 10 hours. Samples were characterized using FTIR, TG/DTA, XRD, DRS, and LCR meter to identify the structure and electrical properties. Some functional groups such as Si-O, Na-O, Fe-O were detected in all samples. XRD analysis showed that the crystalline phase Na2FeSiO4 was formed at 500 °C. Besides, XRD analysis also shows the appearance of impurity phases, such as Na2SiO3 and SiO2. The increasing in sintering temperature causes an increasing in Na2FeSiO4 phase composition in the sample, followed by the rise in the gap energy and a decreasing in the electrical conductivity. Keywords: band energy, crystall structure, electrical conductivity, functional groups, Na2FeSiO4, rice husk silica.

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika 500 ilmu pengetahuan alam dan matematika > 530 Fisika
Program Studi:	FAKULTAS MIPA > Prodi Fisika
Pengguna Deposit:	UPT . Teti Novianti
Date Deposited:	01 Apr 2022 04:51
Terakhir diubah:	01 Apr 2022 04:51
URI:	http://digilib.unila.ac.id/id/eprint/57396

Actions (login required)

Lihat Karya Akhir