PENGARUH PENAMBAHAN ASPAL TERHADAP KARAKTERISTIK TERMAL, STRUKTUR FASA, SIFAT FISIS DAN MEKANIK SILIKA SEKAM PADI

Deafani Wahyu Ardaniswari, 1517041022 (2019) PENGARUH PENAMBAHAN ASPAL TERHADAP KARAKTERISTIK TERMAL, STRUKTUR FASA, SIFAT FISIS DAN MEKANIK SILIKA SEKAM PADI. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

[img]
Preview
File PDF
ABSTRAK-ABSTRACT.pdf

Download (383Kb) | Preview
[img] File PDF
SKRIPSI FULL.pdf
Restricted to Hanya staf

Download (4Mb)
[img]
Preview
File PDF
SKRIPSI TANPA BAB PEMBAHASAN.pdf

Download (3420Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Penelitian dilakukan untuk mengetahui pengaruh penambahan aspal terhadap karakteristik termal, struktur fasa, daya serap air, dan kuat tekan silika yang diekstraksi dari sekam padi menggunakan metode alkalis. Pembuatan paduan silika aspal dilakukan dengan menggunakan perbandingan massa silika dan aspal yaitu 1:0; 1:0,4; 1:0,5; dan 1:0,6 pada suhu pencampuran 160 ̊C dan dipanaskan pada suhu 150 ̊C selama 3 jam. Karakteristik termal dan struktur fasa dianalisis menggunakan Differential Thermal Analysis/Thermo Gravimetrical Analysis (DTA/TGA) dan X-Ray Diffraction (XRD). Hasil analisis DTA/TGA menunjukkan bahwa penambahan aspal mengakibatkan terjadinya penurunan massa, suhu awal (on set), suhu maksimal dan suhu lembah endotermik. Selain itu, terjadi peningkatan suhu puncak eksotermik. Hasil analisis XRD menunjukkan bahwa penambahan aspal mengakibatkan munculnya karbon amorf, terjadi pergeseran 2θ rentang dan intensitas tertinggi dari silika amorf. Penambahan aspal mengakibatkan terjadinya penurunan nilai daya serap air dan kuat tekan. Kata kunci: aspal, karakteristik termal, silika sekam padi, struktur fasa. This research was carried out to investigate the effect of asphalt addition to thermal characteristics, phase structure, water absorption and compressive strength of extracted silica from rice husk using alkaline method. The mass ratio of silica and asphalt alloys were 1:0; 1:0,4; 1:0,5; and 1:0,6. Silica and asphalt were mixed at 160 ̊C followed by calcination at 150 ̊C for 3 hours. Thermal characteristics and phase structures were analyzed using Differential Thermal Analysis/Thermo Gravimetrical Analysis (DTA/TGA) and X-Ray Diffraction (XRD). DTA/TGA analysis results show that the addition of asphalt causes a decreasing in mass, on set temperature, maximum temperature, endothermic temperature, and an increasing in exothermic temperature. The results of XRD analysis show that the addition of asphalt resulted in the appearance of amorphous carbon, shifting the range and the highest intensity of 2θ amorphous silica. The addition of asphalt causes a decrease in the value of water absorption and compressive strength. Keywords: asphalt, phase structure, rice husk silica, thermal characteristics.

Jenis Karya Akhir: Skripsi
Subyek: 500 ilmu pengetahuan alam dan matematika > 530 Fisika
Program Studi: FAKULTAS MIPA > Prodi Fisika
Pengguna Deposit: UPT . Teti Novianti
Date Deposited: 01 Apr 2022 04:51
Terakhir diubah: 01 Apr 2022 04:51
URI: http://digilib.unila.ac.id/id/eprint/57412

Actions (login required)

Lihat Karya Akhir Lihat Karya Akhir