PENGARUH VARIASI TEMPERATUR DAN WAKTU TAHAN REDUKSI DENGAN PENAMBAHAN KONSENTRASI REDUKTOR TERHADAP PENINGKATAN KADAR DAN RECOVERY FERONIKEL MELALUI PROSES REDUKSI SELEKTIF BIJIH NIKEL KADAR RENDAH MENGGUNAKAN ANTRASIT DAN ADITIF MgCl2

Eliyani, 1417041023 (2019) PENGARUH VARIASI TEMPERATUR DAN WAKTU TAHAN REDUKSI DENGAN PENAMBAHAN KONSENTRASI REDUKTOR TERHADAP PENINGKATAN KADAR DAN RECOVERY FERONIKEL MELALUI PROSES REDUKSI SELEKTIF BIJIH NIKEL KADAR RENDAH MENGGUNAKAN ANTRASIT DAN ADITIF MgCl2. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK-ABSTRACT.pdf Download (567Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya staf Download (7Mb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (6Mb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Penelitian ini dilakukan untuk mengetahui pengaruh variasi temperatur dan waktu tahan reduksi dengan penambahan konsentrasi reduktor terhadap peningkatan kadar dan recovery nikel melalui proses reduksi selektif bijih nikel kadar rendah menggunakan antrasit dan aditif MgCl2. Karakterisasi XRF dari konsentrat menunjukkan nilai optimum yaitu pada temperatur 1050°C dengan reduktor 10% dan waktu tahan reduksi selama 120 menit dengan kadar dan recovery nikel sebesar 2,37% dan 56,94%. Pola Difaktogram XRD hasil reduksi selektif menujukkan fasa yang dominan seperti fayalite (Fe2SiO4), magnesioferrite (Fe2MgO4), dan Iron Nickel (FeNi). Ukuran partikel feronikel yang terbentuk sebesar 2,85ηm. Kata Kunci: Feronikel, bijih nikel laterit, seleksi reduksi Increasing weight percent and recovery of nickel with the variation of temperature, reduction holding time, and percentage of reductor on the limonite ore with the antracite and additive MgCl2 by using selective reduction process. According XRF results, the optimum result of the weight percent and recovery nickelis in the temperature 1050°C, 10% reductor, and reduction holding time for 120 minutes those are 2.37wt% and 56.94t%. The dominant phases are fayalite (Fe2SiO4), magnesioferrite (Fe2MgO4), dan ironnickel (Fe dan Ni) with the grain size of ferronickelis 2.85 ηm. Keyword: Ferronickel, limonite, selective reduction, temperature, holding time, reductor, MgCl2.

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika 500 ilmu pengetahuan alam dan matematika > 530 Fisika
Program Studi:	FAKULTAS MIPA > Prodi Fisika
Pengguna Deposit:	UPT . Teti Novianti
Date Deposited:	04 Apr 2022 07:24
Terakhir diubah:	04 Apr 2022 07:24
URI:	http://digilib.unila.ac.id/id/eprint/57458

Actions (login required)

Lihat Karya Akhir