PENGARUH WAKTU PENAMBAHAN DOPING SULFUR TERHADAP LUAS PERMUKAAN DAN STRUKTUR KRISTAL NANOTITANIA MENGGUNAKAN METODE SOL GEL

Anggi Puspita Dewi, 1517041068 (2019) PENGARUH WAKTU PENAMBAHAN DOPING SULFUR TERHADAP LUAS PERMUKAAN DAN STRUKTUR KRISTAL NANOTITANIA MENGGUNAKAN METODE SOL GEL. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

Preview	File PDF 1. ABSTRAK.pdf Download (73Kb) | Preview
	File PDF 2. SKRIPSI FULL.pdf Restricted to Hanya staf Download (4Mb)
Preview	File PDF 3. SKRIPSI FULL TANPA BAB PEMBAHASAN.pdf Download (4Mb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Sintesis titania doping sulfur (S-TiO2) dilakukan dengan metode sol-gel. Titanium isopropoxide (TTIP), tween-80, isopropanol dan asam sulfat (H2SO4) sebagai sumber doping sulfur digunakan sebagai prekursor. Penelitian ini bertujuan untuk mengetahui pengaruh doping sulfur selama 0, 30, 60, 90 dan 120 menit menggunakan pompa injeksi. Bubuk titania dikalsinasi pada 450 °C selama 5 jam. S-doping TiO2 dikarakterisasi menggunakan difraksi sinar-X (XRD) dan luas permukaan (SAA). Hasil XRD menunjukkan bahwa fase yang diperoleh adalah fase anatase untuk semua sampel sedangkan hasil dari SAA menunjukkan bahwa, sampel S-02 memperoleh luas permukaan terbesar yaitu 95,310 m2 /g dan hasil perhitungan dari ukuran partikel dari sampel S-02 diperoleh nilai 10,17 nm. Semakin kecil ukuran partikel yang diperoleh, semakin besar luas permukaan. Kata kunci: Doping sulfur, SAA, titania, XRD. Synthesis of sulfur doping titania (S- TiO2) was carried out by the sol-gel method. Titanium isopropoxide (TTIP), tween-80, isopropanol and asam sulfat (H2SO4) as a source of sulfur doping are used as the of preccursor. This study aims to determine the effect of sulfur doping for 0, 30, 60, 90 and 120 minutes using injection pumps. Titania powder was calcined at 450 °C for 5 hours. S-doping TiO2 was characterized using x-ray diffraction (XRD) and surface area analyzer (SAA). The XRD results showed that the phase obtained was the anatase phase for all samples while the results from the SAA showed that the S-02 sample obtained a surface area the biggest is of 95,310 m2 /g and the results of the calculation of the particle size of the S-02 sample obtained a value of 10,17 nm. The smaller the particle size obtained, the greater the surface area. Keywords: Doping sulfur, SAA, titania, XRD.

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika 500 ilmu pengetahuan alam dan matematika > 530 Fisika
Program Studi:	FAKULTAS MIPA > Prodi Fisika
Pengguna Deposit:	UPT . Teti Novianti
Date Deposited:	04 Apr 2022 07:26
Terakhir diubah:	04 Apr 2022 07:26
URI:	http://digilib.unila.ac.id/id/eprint/57521

Actions (login required)

Lihat Karya Akhir