PENGARUH VARIASI KONSENTRASI BERAT MINERAL BASALT SEBAGAI MATERIAL SUBSTITUSI SEMEN PCC TERHADAP PRODUK MORTAR

Adella Ordiana, 1517041018 (2019) PENGARUH VARIASI KONSENTRASI BERAT MINERAL BASALT SEBAGAI MATERIAL SUBSTITUSI SEMEN PCC TERHADAP PRODUK MORTAR. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

[img]
Preview
File PDF
ABSTRAK-ABSTRACT.pdf

Download (217Kb) | Preview
[img] File PDF
SKRIPSI FULL.pdf
Restricted to Hanya staf

Download (3058Kb)
[img]
Preview
File PDF
SKRIPSI TANPA BAB PEMBAHASAN.pdf

Download (2795Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Telah dilakukan penelitian untuk mengetahui pengaruh variasi konsentrasi berat mineral basalt sebagai material substitusi semen tipe PCC terhadap produk mortar. Bubuk basalt yang digunakan adalah ukuran mesh no.325 dan no.400. Variasi konsentrasi bubuk basalt yaitu sebesar 10, 20, 30, dan 40 (%) dari berat semen PCC. Hasil analisis menunjukkan bahwa basalt memenuhi syarat sebagai material substitusi semen atau pozzolan dengan SiO2+Al2O3+Fe2O3 sebesar 80,116% dan hasil XRD menunjukkan fasa dominan basalt yaitu anorthite, augite, forsterite dan quarts. Nilai kuat tekan tertinggi terdapat pada mortar bubuk basalt mesh no.400 yang di substitusi bubuk basalt 10% sebesar 4,80 MPa diikuti dengan persentase massa jenis sebesar 2,64 g/cm3 , susut bakar sebesar 3,00%, porositas sebesar 1,23% dan absorbsi sebesar 9,53%. Sedangkan nilai kuat tekan mortar standar lebih rendah dibandingkan dengan mortar bubuk basalt mesh no.325 yang disubstitusi bubuk basalt 10% yang sebesar 4,60 MPa, massa jenis sebesar 2,44 g/cm3 , susut bakar sebesar 3,17%, porositas sebesar 1,33% dan absorbsi sebesar 10,05%. Fasa yang dominan terdapat pada mortar semen PCC dengan penambahan bubuk basalt yaitu CASH, quartz, calcite, dan portlandite. Kata kunci: basalt, semen PCC, pozzolan dan mortar Research has been conducted to determine the effect of variations in the concentration of basalt mineral weight as a PCC type cement substitution material for mortar products. Basalt powder used was mesh size no.325 and no.400. The variation of basalt powder concentration is 10, 20, 30, and 40 (%) of the weight of PCC cement. The results of the analysis show that basalt meets the requirements as a substitution material for cement or pozzolan with SiO2+Al2O3+Fe2O3 of 80.116% and XRD results indicate the dominant basalt phase that is anorthite, augite, forsterite and quarts. The highest compressive strength is found in mortar with no.400 basalt mesh powder mortar is substitution of basalt 10% reaching 4.80 MPa followed by a percentage of density of 2,64 g/cm3 , burn shrinkage of 3.00%, porosity of 1.23% and absorption of 9, 53%. While the standard compressive strength of mortar is lower that of basalt mesh powder no.325 which is substituted for 10% of 4.60 MPa, density of 2.44 g/cm3 , burn shrinkage of 3.17%, porosity of 1.33% and absorption of 10 .05%. The dominant phase is found in PCC cement mortar with the addition of basalt powder that is CASH, quartz, calcite, and portlandite. Keywords: basalt, cement PCC, pozzolan and mortar

Jenis Karya Akhir: Skripsi
Subyek: 500 ilmu pengetahuan alam dan matematika
500 ilmu pengetahuan alam dan matematika > 530 Fisika
Program Studi: FAKULTAS MIPA > Prodi Fisika
Pengguna Deposit: UPT . Teti Novianti
Date Deposited: 04 Apr 2022 07:27
Terakhir diubah: 04 Apr 2022 07:27
URI: http://digilib.unila.ac.id/id/eprint/57547

Actions (login required)

Lihat Karya Akhir Lihat Karya Akhir