SINTESIS DAN KARAKTERISASI SILIKA SEKAM PADI DENGAN MENGGUNAKAN METODE PENGENDAPAN

An’nisa Irnanda Abidin, 1417041010 (2019) SINTESIS DAN KARAKTERISASI SILIKA SEKAM PADI DENGAN MENGGUNAKAN METODE PENGENDAPAN. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK.pdf Download (113Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya staf Download (2922Kb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (2922Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Penelitian ini dilakukan untuk mendapatkan silika dari bahan dasar sekam padi dengan menggunakan metode pengendapan. Proses leaching digunakan pada penelitian ini untuk preparasi bahan dasar. Sampel yang telah di-leaching tersebut kemudian disintesis dengan metode pengendapan. Kemudian sampel dikalsinasi pada suhu 700 oC selama 5 jam lalu dikarakterisasi. Analisis XRF menghasilkan silika tertinggi sebesar 96,824 % pada sampel yang disintesis dengan metode pengendapan. Hasil DTA menunjukkan adanya puncak-puncak endotermik pada suhu 73 °C, 393 °C, 470 °C dan 883 °C masing-masing terjadinya penguapan air, pembakaran karbon dan bahan-bahan volatil lainnya dan transformasi fase tridimit. Sedangkan hasil TGA menunjukkan total penyusutan massa sebesar 19,23 % dari massa awal. Analisis XRD menghasilkan puncak tertinggi pada 2 masing-masing sebesar 21,77o , 23,26o , dan 23,28o menunjukkan silika berfase amorf. Hasil analisis FTIR ketiga sampel memiliki gugus fungsi -OH, Si-OH, Si- O-Si, Si-O, dan O-Si-O. Gugus fungsi Si-O-Si muncul pada ketiga sampel menunjukkan karakteristik silika. Hasil analisis SEM dari ketiga sampel menunjukkan struktur permukaan dan bentuk yang menggumpal dan tidak beraturan. Sedangkan hasil EDX diperoleh unsur yang terbentuk adalah Si dan O pada ketiga sampel. Kata kunci: Sekam padi, silika, pengendapan, kalsinasi, XRF, DTA-TGA, XRD, FTIR, dan SEM-EDX. This research was conducted to get silica from rice husk as raw material by precipitation method. Leaching process were used in this study to raw material preparation. Samples were leached and then synthesized by precipitation method. This samples calcined at temperature 700 oC for 5 hour and characterized. Analysis XRF shown the highest silica of 96,824 % in samples synthsized by precipitation method. The results of DTA showed the presence of endothermic peaks at temperatures 73 °C, 393 °C, 470 °C and 883 °C for evaporation of water, carbon combustion and other volatile materials and transformation tridymite phase, respectively. While the TGA results show total mass shrinkage up to 19,23 % from initial mass. Analysis XRD for three samples results a strong broad peak at 2 = 21,77o , 23,26o , dan 23,28o assosiated with amorphous silica, respectively. Analysis FTIR shown that three samples have functional groups -OH, Si-OH, Si- O-Si, Si-O, and O-Si-O. The Si-O-Si function group appeared in three samples showing the characteristics of silica. The results of SEM analysis of the three samples showed a surface structure and a agglomerate and irregular shape. While the EDX results obtained elements formed are Si and O on all three samples. Keywords: Rice husk, silica, precipitation, calcination, XRF, DTA-TGA, XRD, FTIR, and SEM-EDX.

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika 500 ilmu pengetahuan alam dan matematika > 530 Fisika
Program Studi:	FAKULTAS MIPA > Prodi Fisika
Pengguna Deposit:	UPT . Teti Novianti
Date Deposited:	02 Apr 2022 22:45
Terakhir diubah:	02 Apr 2022 22:45
URI:	http://digilib.unila.ac.id/id/eprint/57557

Actions (login required)

Lihat Karya Akhir