PENGARUH SUHU DAN WAKTU PEMANASAN TERHADAP ANALISIS DAN UJI FISIS GERABAH (Skripsi)

Latifah Desti Lustikasari , 1317041021 (2019) PENGARUH SUHU DAN WAKTU PEMANASAN TERHADAP ANALISIS DAN UJI FISIS GERABAH (Skripsi). FAKULTAS ILMU KEGURUAN DAN ILMU PENDIDIKAN, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK.pdf Download (153Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya staf Download (2597Kb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (2598Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Penelitian ini bertujuan untuk mengetahui kakrakterisitik dan kualitas gerabah komposisi 65% mineral lempung dan 35% mineral feldspar. Sampel gerabah dipanaskan pada variasi suhu 800ºC, 900ºC, 950ºC dan 1000ºC dan waktu 2, 3, 4 dan 5 jam. Hasil yang diperoleh menunjukkan bahwa nilai densitas=2,28 gram/cm3 dan kuat tekan=8,96Mpa optimum pada waktu tahan 3 jam suhu 1000ºC. Nilai uji absorbsi dan porositas menurun seiring naiknya suhu pemanasan. Berdasarkan karakterisasi XRF bahan baku gerabah mengandungan unsur Si=56,405% dan Al=18,927%. Hasil uji XRD waktu pemanasan 3 jam variasi suhu 800-1000ºC puncak fasa tertinggi didominasi quartz (PDF-461045) dengan rentan puncak 2θ(26º-28,7º). Fasa lain yang terbentuk yaitu cristobalite (PDF-391425) dan tridymite (PDF-421401). Mulai suhu 900ºC terjadi ikatan Al2SiO5 fasa sillimanite (PDF-380471). Kata kunci: feldspar, gerabah, sifat fisis, XRD, XRF This study aims to know the characteristics and quality of pottery with the composition of 65% clay and 35% feldspart mineral. Pottery samples were heated at temperature variations of 800ºC, 900ºC, 950ºC and 1000ºC and time 2, 3, 4 and 5 hours. The results obtained showed that the density value=2,28 gram/cm3 and compressive srength=8,96 Mpa optimum in 3 hour time heating and 1000ºC temperature. The value of absorbtion and porosity decreases with increasing heating temperature. Based on XRF characterization pottery containing Si=56,405% and Al=18,927%. The XRD test at 800-1000ºC temperature and 3 hour time heating was domination with quartz phase (PDF-461045) at 2θ(26º28,7º) peak. Another phase was formed are cristobalite (PDF-391425) dan tridymite (PDF-421401). Starting at 900ºC Al2SiO5 was bonding sillimanite phase (PDF-380471). Keywords: feldspart, pottery, physical properties, XRD, XRF

Jenis Karya Akhir:	Skripsi
Subyek:	300 Ilmu sosial > 370 Pendidikan 500 ilmu pengetahuan alam dan matematika > 540 Kimia dan ilmu yang berhubungan
Program Studi:	FKIP > Prodi Pendidikan Kimia
Pengguna Deposit:	UPT . Teti Novianti
Date Deposited:	18 Apr 2022 03:17
Terakhir diubah:	18 Apr 2022 03:17
URI:	http://digilib.unila.ac.id/id/eprint/59173

Actions (login required)

Lihat Karya Akhir