ANALISIS PENGARUH KONSENTRASI LARUTAN AIR GARAM (NaCl) PADA SAAT PROSES QUENCHING TERHADAP STRUKTUR MIKRO DAN KEKERASAN BAJA KARBON ST 37 ( C = 0, 303 %)

Agus Supriadi, 1517041107 (2021) ANALISIS PENGARUH KONSENTRASI LARUTAN AIR GARAM (NaCl) PADA SAAT PROSES QUENCHING TERHADAP STRUKTUR MIKRO DAN KEKERASAN BAJA KARBON ST 37 ( C = 0, 303 %). FAKULTAS MATEMATIKA ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK - Agus Supriadi.pdf Download (553Kb) | Preview
	File PDF SKRIPSI FULL - Agus Supriadi.pdf Restricted to Hanya staf Download (4Mb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN - Agus Supriadi (1).pdf Download (4Mb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Telah dilakukan penelitian terkait analisis pengaruh konsentrasi larutan air garam (NaCl) pada saat proses quenching terhadap kekerasan dan struktur mikro pada baja karbon ST 37 (C = 0,303 %). Penelitian ini dilakukan dengan metode hardening dengan pemanasan awal Pre-heating pada suhu 600 oC selama 30 menit dan austenisasi pada suhu 850 oC selama 25 menit. Selanjutnya sampel di quenching pada media larutan garam 0%, 5%, 10%, dan 15%. Dengan pengujian menggunakan metode Spark-OES diketahui bahawa sampel memiliki konsentrasi unsure karbon sebesar 0,303%. Pada penelitian yang dilakukan diketahuikon sentrasi larutan garam berpengaruh 71,73% terhadap kekerasan dan 45,03% terhadap ketangguhan baja karbon menengah. Selain itu proses hardening yang diakukan mengakibatkan transformasi fasa dari ferrit (α) dan perlit menjadi martensit. Kata kunci: Hardening, pre-heating, quenching, ferrit, martensit Research has been carried out related to the analysis of the effect of the concentration salt solution (NaCl) during the quenching on hardness and microstructure of ST 37 (C = 0, 303 %) carbon steel. This research was conducted by using the hardening method with pre-heating at 600 oC for 30 minutes and austenizing at 850oC for 25 minutes. Furthermore, the samples were quenched in salt solution media of 0%, 5%, 10%, and 15%. By testing using the Spark-OES method, it is known that the sample has a carbon element concentration of 0.303%. In the research, it was found that the concentration of salt solution had an effect of 71.73% to the hardness and 45,03% to the toughness of medium carbon steel. In addition, the hardening process resultes in a phase transformation from ferrite (α) and pearlite to martensite. Keyword: Hardening, pre-heating, quenching, ferrit, martensite

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika 500 ilmu pengetahuan alam dan matematika > 530 Fisika
Program Studi:	FAKULTAS MIPA > Prodi Fisika
Pengguna Deposit:	UPT . Teti Novianti
Date Deposited:	20 Apr 2022 07:16
Terakhir diubah:	20 Apr 2022 07:16
URI:	http://digilib.unila.ac.id/id/eprint/60098