PENGARUH PENAMBAHAN NH4OH TERHADAP PEMBENTUKAN NANOTITANIA PADA TEMPERATUR 2500C

ANGGI DESNITA SARI, 1617041005 (2021) PENGARUH PENAMBAHAN NH4OH TERHADAP PEMBENTUKAN NANOTITANIA PADA TEMPERATUR 2500C. FAKULTAS MATIMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK - anggi desnita.pdf Download (1921Kb) | Preview
	File PDF SKRIPSI FULL - anggi desnita.pdf Restricted to Hanya staf Download (2203Kb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN - anggi desnita.pdf Download (2202Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Telah dilakukan penelitian mengenai sintesis nanotitania dari bahan utama TiOSO4 dengan metode hidrotermal. Pada penelitian ini dibuat 5 sampel penelitian dengan menggunakan variasi konsentrasi NH4OH. Sampel yang telah dibuat dilakukan uji SEM dan XRD. Hasil uji XRD dianalisis secara kualitatif dan kuantitatif. Analisis kualitatif dilakukan menggunakan prangkat lunak High Score Plus (HSP) dengan mecocokkan pola difraksi hasil uji dengan pola difraksi pada database dengan Search Match sehingga, diperoleh hasil bahwa sampel dengan penambahan NH4OH 6, 8, 10, dan 12% terbentuk fasa anatase, rutil dan brukit. Sementara, pada sampel dengan penambahan NH4OH 14% hanya terbentuk fasa anatase dan rutil. Analisis kuantitatif dilakukan menggunakan perangkat lunak Rietica dengan penghalusan metode Rietveld. Hasil identifikasi diperoleh bahwa penambahan NH4OH berpengaruh terhadap persen berat dan ukuran partikel dari masing-masing fasa. Semakin tinggi konsentrasi NH4OH maka semakin besar nilai dari persen berat dari fasa anatase, rutil maupun brukit. Semakin tinggi konsentasi NH4OH maka semakin besar ukuran partikel dari fasa anatase dan rutil. Identifikasi gambar hasil uji SEM diperoleh bahwa pola gambar memiliki struktur yang kasar berupa bongkahan-bongkahan menyerupai batu karang, ukuran partikel yang tidak seragam, adanya daerah terang dan gelap serta letak partikel yang tidak beraturan. Kata kunci: Nanotitania, hidrotermal, NH4OH, TiOSO4. Research has been carried out on the synthesis of nano titania from the main ingredient TiOSO4 using the hydrothermal method. In this study, Five research samples were made using variations in the concentration of NH4OH. The samples that have been made are tested for SEM and XRD. The results of the XRD test were analyzed qualitatively and quantitatively. Qualitative analysis was carried out using High Score Plus (HSP) software by matching the diffraction pattern of the test results with the diffraction pattern in the database with Search Match that, the results obtained that samples with the addition of NH4OH 6, 8, 10, and 12% formed anatase, rutile and rutile phases, brookite. Meanwhile, in the sample with the addition of 14% NH4OH only anatase and rutile phases were formed. The quantitative analysis does use Rietica software with the Rietveld refinement method. The identification results showed that the addition of NH4OH affected the weight percent and particle size of each phase. The higher concentration of NH4OH, the greater the value of the percent by weight of the anatase, rutile, and brookite phases. The higher the concentration of NH4OH, the larger the particle size of the anatase and rutile phases. The image identification from the SEM test results showed that the image pattern has a rough structure in the shape form of chunks resembling rocks, non-uniform particle size, the presence of light and dark areas, and irregular particle locations. Keyword: Nano titania, hydrothermal, NH4OH, TiOSO4.

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika > 530 Fisika
Program Studi:	FAKULTAS MIPA > Prodi Fisika
Pengguna Deposit:	UPT . Rukiah
Date Deposited:	21 Apr 2022 04:35
Terakhir diubah:	21 Apr 2022 04:35
URI:	http://digilib.unila.ac.id/id/eprint/60249

Actions (login required)

Lihat Karya Akhir