SINTESIS DAN KARAKTERISASI ZEOLITE SOCONY MOBILE-5 (ZSM-5) PORI HIRARKI BERBASIS SILIKA ABU AMPAS TEBU MENGGUNAKAN PATI SEBAGAI BIO-MESOPOROGEN

NURMALIA SALIS, 1717011080 (2022) SINTESIS DAN KARAKTERISASI ZEOLITE SOCONY MOBILE-5 (ZSM-5) PORI HIRARKI BERBASIS SILIKA ABU AMPAS TEBU MENGGUNAKAN PATI SEBAGAI BIO-MESOPOROGEN. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK.pdf Download (2706Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya staf Download (2707Kb)
Preview	File PDF SKRIPSI TANPA PEMBAHASAN.pdf Download (2706Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

ZSM-5 pori hierarki telah berhasil disintesis dari abu ampas tebu melalui metode hidrotermal dengan penambahan pati sebagai agen pengarah mesopori. Penelitian diawali dengan ekstraksi silika SCBA menggunakan pelarut NaOH dan dilanjutkan dealuminasi menggunakan asam klorida. Silika SCBA yang diperoleh dikarakterisasi dengan X-ray diffraction (XRD), Fourier Transform Infrared (FTIR), X-ray fluorescence (XRF). Hasil karakterisasi menunjukkan silika SCBA didominasi oleh fasa amorf, mengandung gugus silanol dan siloksan serta dealuminasi berhasil meningkatkan rasio Si/Al menjadi 50,2. Kemudian Silika SCBA digunakan sebagai prekursor sintesis ZSM-5. Proses sintesis ZSM-5 hierarki dilakukan variasi rasio Si/Al silika SCBA (1,97; 50,2), metode preparasi gel, waktu kristalisasi (96; 144 jam) dan jumlah pati (5; 10%) dengan penambahan benih silikalit. Produk yang telah disintesis dikarakterisasi menggunakan XRD dan BET surface area analyzer. Hasil padatan ZSM-5 yang disintesis selama 144 jam pada 180°C menggunakan pati sebanyak 10% menunjukkan kristalinitas tertinggi dan terkonfirmasi memiliki pori hierarki dengan pori meso sebesar 2,5 nm yang seragam dengan luas permukan meso 27 m2/g. Kata Kunci: Abu ampas tebu, ekstraksi silika, pati, bio-mesoporogen, ZSM-5 pori hierarki, ZSM-5 hierarchical has been successfully synthesized from sugarcane bagasse ash (SCBA) by hydrothermal method with the addition of starch as a mesoporous directing agent. The study began with the extraction of SCBA silica using NaOH solvent and continued with dealumination using hydrochloric acid. The obtained SCBA silica was characterized by X-ray diffraction (XRD), Fourier Transform Infrared (FTIR), X-ray fluorescence (XRF). The characterization results showed that SCBA silica was dominated by an amorphous phase, containing silanol and siloxane groups and dealumination succeeded in increasing the Si/Al ratio to 50.2. Then Silica SCBA was used as a precursor for the synthesis of ZSM-5. The hierarchical ZSM-5 synthesis process was carried out by varying the ratio of Si/Al silica SCBA (1.97; 50.2), gel preparation method, crystallization time (96; 144 hours) and amount of starch (5; 10%) with the addition of silicalite seeds. The synthesized product was characterized using XRD and BET surface area analyzer. The solid yield of ZSM-5 which was synthesized for 144 hours at 180°C using 10% starch showed the highest crystallinity and was confirmed to have hierarchical pores with a meso pore of 2.5 nm which was uniform with a meso surface area of 27.92 m2/g. Keywords: Sugarcane baggase ash, silica extraction, starch, bio-mesoporogen, ZSM-5 hierarchical pore.

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika 500 ilmu pengetahuan alam dan matematika > 540 Kimia dan ilmu yang berhubungan
Program Studi:	FAKULTAS MIPA > Prodi Kimia
Pengguna Deposit:	2203295186 . Digilib
Date Deposited:	22 Apr 2022 06:17
Terakhir diubah:	22 Apr 2022 06:17
URI:	http://digilib.unila.ac.id/id/eprint/60398

Actions (login required)

Lihat Karya Akhir